Oxygen Content and Thermodynamic Stability of YBaCo2O6−δ Double Perovskite

الملخص EN

The thermodynamic stability of the double perovskite YBaCo2O6−δ was studied using the coulometric titration technique and verified by measurements of the overall conductivity depending on oxygen partial pressure at a given temperature.

As a result, the stability diagram of YBaCo2O6−δ was plotted.

YBaCo2O6−δ was found to be thermodynamically stable in air at 850°C and higher temperatures, whereas its thermodynamic stability at 900°C is limited by the range of oxygen partial pressures −3.56 ≤ log(pO2/atm) ≤ −0.14.

Oxygen content in YBaCo2O6−δ slightly decreases at 900°C from 5.035 at log(pO2/atm) = −0.14 to 4.989 in the atmosphere with log(pO2/atm) = −3.565 indicating a crucial role which variation of Co+3/Co+2 ratio plays in its stability.

YBaCo2O6−δ decomposes into the mixture of YCoO3 and BaCoO3−z at the high pO2 stability limit, whereas YBaCo4O7, BaCo1−xYxO3−γ, and Y2O3 were identified as the products of its decomposition at the low pO2 one.