Effect of die’s shape, sheet thickness and type of alloy on the springback phenomenon

الملخص EN

In this paper the effect of the spring back on the bending operation of different materials and alloys have been studied.

Dies were designed and constructed in different shape (U-die, V-die) for several sheet’s thickness.

Two types of alloys were used; Aluminum Alloy 7020 T6 and Brass Alloy.

These alloys have different sheet thickness (2, 4, 6 and 8) mm.

Aluminum alloys are heated to 270 °C and 330˚C with cooling in the furnace for 90 min.

while the brass alloys heated to 300, 320, 340 and 420 °C with cooling for 2 hours in furnace.

Bending was done by using the press of 80 ton.

The spring back is calculated by published equation.

It can be concluded that, the spring back phenomenon caused to enlarge the external dimensions when releasing the load and thick material have less spring back due to the enlarge of the plastic deformation.

It’s found that the die’s shapes have great effect on the spring back, and when the temperature of the specimen is increased, caused decreased in the springbuck.