تصنيع طابوق حراري من خام الفلنت العراقي
العناوين الأخرى
Manufacturing of refractory bricks from Iraqi flint
المؤلف
المصدر
العدد
المجلد 35، العدد (s1) (31 ديسمبر/كانون الأول 2017)، ص ص. 161-171، 11ص.
الناشر
تاريخ النشر
2017-12-31
دولة النشر
العراق
عدد الصفحات
11
التخصصات الرئيسية
العلوم الهندسية والتكنولوجية (متداخلة التخصصات)
الملخص AR
It was done in this study the preparation of bricks refractory from Iraqi Flint and adding Iraqi white kaolin as a binding material in ratio (25, 30, 35, 40, 45)%.
The samples were formed by dry pressing, dried at room temperature for 24hr then at (110)̊C for 6hr then fired at (1200)˚C with soking time for 2hr.
Linear shrinkage, Apparent density, Porosity, water absorption and microstructure by (SEM) as physical properties, diametrical strength and surface roughness as mechanical testing, and thermal conductivity, linear thermal expansion and thermal shock resistance as thermal properties were studied in this study.
According to (SEM) and (XRD) results, the refractories consist of mullite phase and glass phase.
The results show the increase of linear shrinkage and decrease of apparent porosity and water absorption with the increasing of kaolin adding because of the increasing of ceramic raw material, which mean increasing of glass phase.
For the same reason linear thermal expansion increase with the kaolin adding increasing
الملخص EN
It was done in this study the preparation of bricks refractory from Iraqi Flint and adding Iraqi white kaolin as a binding material in ratio (25, 30, 35, 40, 45)%.
The samples were formed by dry pressing, dried at room temperature for 24hr then at (110)̊C for 6hr then fired at (1200)˚C with soking time for 2hr.
Linear shrinkage, Apparent density, Porosity, water absorption and microstructure by (SEM) as physical properties, diametrical strength and surface roughness as mechanical testing, and thermal conductivity, linear thermal expansion and thermal shock resistance as thermal properties were studied in this study.
According to (SEM) and (XRD) results, the refractories consist of mullite phase and glass phase.
The results show the increase of linear shrinkage and decrease of apparent porosity and water absorption with the increasing of kaolin adding because of the increasing of ceramic raw material, which mean increasing of glass phase.
For the same reason linear thermal expansion increase with the kaolin adding increasing
نمط استشهاد جمعية علماء النفس الأمريكية (APA)
هادي، إيناس محيي. 2017. تصنيع طابوق حراري من خام الفلنت العراقي. مجلة الهندسة والتكنولوجيا،مج. 35، ع. (s1)، ص ص. 161-171.
https://search.emarefa.net/detail/BIM-877828
نمط استشهاد الجمعية الأمريكية للغات الحديثة (MLA)
هادي، إيناس محيي. تصنيع طابوق حراري من خام الفلنت العراقي. مجلة الهندسة والتكنولوجيا مج. 35، العدد الخاص الأول (2017)، ص ص. 161-171.
https://search.emarefa.net/detail/BIM-877828
نمط استشهاد الجمعية الطبية الأمريكية (AMA)
هادي، إيناس محيي. تصنيع طابوق حراري من خام الفلنت العراقي. مجلة الهندسة والتكنولوجيا. 2017. مج. 35، ع. (s1)، ص ص. 161-171.
https://search.emarefa.net/detail/BIM-877828
نوع البيانات
مقالات
لغة النص
العربية
الملاحظات
يتضمن ملحق : ص. 171
رقم السجل
BIM-877828
قاعدة معامل التأثير والاستشهادات المرجعية العربي "ارسيف Arcif"
أضخم قاعدة بيانات عربية للاستشهادات المرجعية للمجلات العلمية المحكمة الصادرة في العالم العربي
تقوم هذه الخدمة بالتحقق من التشابه أو الانتحال في الأبحاث والمقالات العلمية والأطروحات الجامعية والكتب والأبحاث باللغة العربية، وتحديد درجة التشابه أو أصالة الأعمال البحثية وحماية ملكيتها الفكرية. تعرف اكثر