تحسين متانة العزل الكهربائي لمتراكب الكاؤلين العراقي بإضافة الزركونيا المايكروية و النانوية

Abstract EN

Iraqi kaolin as a matrix material is used as a principle part of the study after additives sugarcane straw in ratio (10%) and (2%) Poly Vinyl Alcohol ( PVA) as a binding material.

(Micro or Nano) Zirconia has been added to the composite in different ratio ( 0% , 5 % , 10% , 15% , 20%) for the purpose of improving thermal properties.

Samples are formed in a semi-dry pressing with pressure of about (25 Mpa).

The formulation is achieved by using a template of (12 mm) diameter and a time of about (2 min).

Then, the prepared samples have been sintered.

Burning process was carried out by three temperature degrees ( 1000, 1100, 1200 ) Co for mean raise about 3 temperature degree / 1 minute and remained at every temperature degree for two hours.

The results showed that the increase in the proportion of ( Micro or Nano ) Zirconia results in increasing the value of dielectric strength and the best results where achieved by adding Nano Zirconia.

The increasing of the burning temperature also leads to increase the value of the dielectric strength.