The effect of PVP addition on the mechanical properties of [84%LLDPE : 15 % ( 100- X) %PP: X%PVP) : 1%Basalt Particle] Polymer Blend Composites
Other Title(s)
) دراسة تأثير إضافة PVP) المتراكب البوليمري للخيط الميكانيكية الخواص على : [84 % LLDPE : 15 % (100-X) % PP : X % PVP) : 1 % basalt particle]
Joint Authors
al-Shaliji, Sihama Isa Salih
Jabur, Akram Rahim
Muhammad, Tayyib A.
Source
Engineering and Technology Journal
Issue
Vol. 32, Issue 3A (31 Mar. 2014), pp.573-585, 13 p.
Publisher
Publication Date
2014-03-31
Country of Publication
Iraq
No. of Pages
13
Main Subjects
Engineering & Technology Sciences (Multidisciplinary)
Topics
Abstract AR
حضرت المتراكبات ذات أساس الخليط البوليمري الثلاثي, و فق الصيغة [84%LLDPE:15%((100-X)%PP:X%PVP):1%B.P] و بنسب وزنية مختارة لقيم X 16, 12 (%0, 4, 8).
و قد تم تحضيرها بشكل شرائط حضرت بعملية البثق بواسطة باثقة ثنائية اللولب و استخدمت عملية كبس الأشرطة لتحضير العينات وفق المواصفة القياسية (ASTM), درست الفحوصات الميكانيكية للعينات المحضرة و المتمثلة (فحص الشد و الانحناء و الانضغاط و الصدمة و الصلادة و الزحف) أظهرت النتائج زيادة في الخصائص الميكانيكية مع زيادة نسبة PVP باستثناء المطيلية و علاوة على ذلك سجلت النتائج أعلى قيم لمقاومة الشد, معامل المرونة, مقاومة الانضغاط و مقاومة الانحناء و أعلى إجهاد قص و معامل مرونة الانحناء و معامل الزحف عند نسبة (8% wt) PVP و هي على الترتيب (31.32MPa, 0.14GPa, 27.4MPa, 0.6MPa, 1.08GPa, 0.558GPa) في حين سجلت أعلى قيم لمتانة الصدمة و قيم الصلادة عند نسبة PVP (12% wt.) (1.696 Pa√m) و 4%wt (56.5) على الترتيب.
Abstract EN
Polymer blends composites were prepared according to the formula [84 % LLDPE : 15 % ((100-X) % PP : X % PVP) : 1 %B.P] with weight ratios selected for X values (0,4,8,12,16 %), as strips by double screw extruder and use press process the strips to prepare the samples according ASTM specification, the mechanical properties were studied for all the prepared samples which are (tensile, flexural, compression, impact, hardness, and creep tests).
The results are as following :- results showed increment of mechanical properties as PVP ratio increases except elongation, furthermore the results recorded highest values of fracture strength, young modulus, compressive strength, flexural strength, maximum shear stress, flexural modulus and creep modulus at PVP 8 % wt.
which are (31.32MPa, 0.14GPa, 27.4MPa,24MPa, 0.6MPa, 1.08GPa and 0.558GPa) respectively.
While the highest values of fracture toughness and hardness recorded at 12 % wt.
(1.4696Pa m), and at 4 % wt.
(56.5) respectively.
American Psychological Association (APA)
al-Shaliji, Sihama Isa Salih& Jabur, Akram Rahim& Muhammad, Tayyib A.. 2014. The effect of PVP addition on the mechanical properties of [84%LLDPE : 15 % ( 100- X) %PP: X%PVP) : 1%Basalt Particle] Polymer Blend Composites. Engineering and Technology Journal،Vol. 32, no. 3A, pp.573-585.
https://search.emarefa.net/detail/BIM-371171
Modern Language Association (MLA)
Muhammad, Tayyib A.…[et al.]. The effect of PVP addition on the mechanical properties of [84%LLDPE : 15 % ( 100- X) %PP: X%PVP) : 1%Basalt Particle] Polymer Blend Composites. Engineering and Technology Journal Vol. 32, no. 3A (2014), pp.573-585.
https://search.emarefa.net/detail/BIM-371171
American Medical Association (AMA)
al-Shaliji, Sihama Isa Salih& Jabur, Akram Rahim& Muhammad, Tayyib A.. The effect of PVP addition on the mechanical properties of [84%LLDPE : 15 % ( 100- X) %PP: X%PVP) : 1%Basalt Particle] Polymer Blend Composites. Engineering and Technology Journal. 2014. Vol. 32, no. 3A, pp.573-585.
https://search.emarefa.net/detail/BIM-371171
Data Type
Journal Articles
Language
English
Notes
Includes bibliographical references : p. 583-585
Record ID
BIM-371171