γ-Rays Irradiation Induced Structural and Morphological Changes in Copper Nanowires

Abstract EN

This contribution reports on the effect of γ-irradiations on the structural and morphological properties of copper nanowires (Cu-NWs) within the γ doses varying from 6 to 25 kGy.

At 9 kGy, the Cu-NWs started welding, forming perfect X-, V-, II-, and Y-shaped molecular junctions.

Further increasing the γ dose up to 15 kGy caused the Cu-NWs to fuse and form larger diameter NWs.

At the highest dose of 25 kGy, the nanowires converted into a continuous Cu thin film.

However, X-ray diffraction (XRD) results showed that the structure of the Cu-NWs remained stable even after converting into a thin film.

The formation of the Cuprite (Cu2O) phases was observed at higher γ dose.

The mechanism of forming welded networks of Cu-NWs and Cu thin films is explained via the short and high energy γ-ray wavelengths which act on Cu-Cu molecular covalent bonds isotropically.