دراسة الموصلية الحرارية و مقاومة الصدمة لمادة البولي أستر غير المشبع المقواة بدقائق من الألمنيوم

Abstract EN

This work aims to prepare a polymer – metallic (composite material) reinforced by aluminum particles with different grain size and various volume fraction.

Using filing particles from aluminum with a grain size (13 μm), and aluminum dust particles.

This work studies the effect of volume fraction for aluminum particles and predicts its effect on thermal conductivity and impact strength of the prepared composite material.

The results show that the thermal conductivity of a material reinforced by aluminum particles (filings) increases as the volume - fraction increases, where it reaches (4.85 W/mm.K) at volume – fraction (9.2 %), whereas in composite material reinforced by aluminum dust, the thermal conductivity increases to reach (4.74 W/mm.K) at volume – fraction (2.2 %) and then decrease to (4.38 W/mm.K ) at volume fraction ( 4.7% ) and then stable at limited ratio from volume fraction.

Also the results show that the mechanical impact resistance for composite materials by dust particle increases as the volume – fraction – particle increases, where it reaches (81.25 kJ/m2) at volume fraction ( 9.2% ).

whereas composite materials reinforced with aluminum particle (filing) also increase as volume – fraction increases, but, as little as the increasing of composite materials reinforced by dust where reachs (63.158 kJ/m2 ) at volume fraction ( 9.2 % ).