تأثير المعاملة الحرارية الجزئية على الخواص الميكانيكية لصلب العدة عالي الكربون المستخدم في صناعة الأجزاء الفعالة لقوالب القطع على البارد
Other Title(s)
Effect of partial heat treatment on the mechanical properties of high carbon tool steel used in manufacturing active parts in cold work tool steel dies
Author
Source
Issue
Vol. 27, Issue 05 (30 Apr. 2009), pp.180-189, 10 p.
Publisher
Publication Date
2009-04-30
Country of Publication
Iraq
No. of Pages
10
Main Subjects
Topics
Abstract AR
تم إجراء المعاملة الحرارية الجزئية و دراسة تأثيرها على الخواص الميكانيكية لصلب العدة عالي الكربون في هذا البحث.
استخدمت سبيكة الفولاذ عالي الكربون نوع (X210Cr12) و المصنفة بالرقم (1.2080) حسب نظام ال (DIN) الألماني في تشغيل عينات بأبعاد (5×44×20) ملم تم عزل العينات من المنتصف بواسطة نوعين من غلاف عازل، إذ تم عزل (18) عينة بواسطة غلاف من الكرافيت بسمك (5ملم), وعزلت (18) عينة أخرى بواسطة غلاف من مادة سيراميكية (الومينا + كاؤولين) بسمك (5 ملم), و أجريت المعاملة الحرارية للسطح الغيرمعزول (من المنتصف إلى الحد القاطع (Sharp edge)) بالتسخين التدريجي، إذ تبين عند التسخين إلى درجة حرارة (980 oC) يتم الحصول على أعلى قيمة للصلادة (HRC 65) بعد اجراء عملية الإخماد بالزيت (Quenching in oil) و تمت دراسة عملية إزالة الإجهادات (Stress relives) إذ تبين عند التسخين إلى درجة حرارة مابين (100-200 oC) لم يطرأ تغيير كبير على قيمة الصلادة و أدت العملية إلى زيادة المتانة بشكل ملحوظ.
و انخفضت الصلادة إلى أدنى معدل لها و هي (HRC 30) عند التسخين إلى درجة حرارة 600oC)) أجري اختبار صلادة روكويل (HRC) لعينات البحث حيث تم تحديد أربع نقاط على سطح كل عينة، تبعد النقطة الأولى بمسافة (10 ملم) عن الحد القاطع و النقطة الثانية (20 ملم) عن الحد القاطع ضمن السطح الغير معزول و النقطة الثالثة (30 ملم) و النقطة الرابعة (40 ملم) عن الحد القاطع ضمن السطح المعزول و سجلت قيم الصلادة (65,64 HRC), من الحد القاطع إلى المنتصف ضمن السطح الغير معزول و (48,47 HRC) ضمن السطح المعزول بالنسبة للعينات المعزولة بغلاف كرافيتي .
أما العينات المعزولة بغلاف سيراميكي فقد سجلت قيم الصلادة (65,64 HRC) من الحد القاطع إلى المنتصف للسطح الغير معزول و (51,52 HRC) من المنتصف إلى نهاية العينة ضمن السطح المعزول.
تم ملاحظة تقارب قيم الصلادة للعينات المعزولة بغلاف كرافيتي و العينات المعزولة بغلاف سيراميكي.
تم إجراء المعاملة الحرارية الجزئية الذي تم التوصل اليها من خلال البحث للأجزاء الفعالة ((ذكر و انثى القالب Punch &Die) لقوالب القطع و القوالب المرحلية التي ينتجها معمل القوالب و العدد المركزي/ شركة نصر العامة للصناعات الميكانيكية، حيث تم ملاحظة زيادة عمر الأجزاء المذكورة و زيادة مقاومتها للكسر تحت ظروف العمل المختلفة.
Abstract EN
Effect of partial heat treatment on the mechanical properties of high carbon tool steel used in manufacturing active parts in cold work tool steel dies was investigated in this work.
High carbon alloy steel (X210Cr12) classified as (QN1.2080) according to (DIN) was used for machining specimens with dimensions (5×44×20mm).
(18) specimens were insulated from the middle to the end by graphite with (5mm) thickness and (18) specimens were insulated by ceramic (Al2O3 + Kaolin) with (5mm) thickness.
The distance between the middle to the sharp edge was not insulated.
All these specimen were subjected to heat treatment, They show that can obtain hardness (65HRC) for the sharp edge at (980oC) after the specimens were quenched in oil.
Stress relive was subjected to all specimens , it has been shown during heating between (100-200oC) There is no big effect on the hardness and the strength was increased, also when heating temperature increase up to (600 C ) the hardness decrease at (30 HRC) .
Rockwell hardness test was employed to all specimens, at four locations for each specimen.
The first location is at distance (10mm) from the sharp edge and the second at (20mm) from the sharp edge within un insulated part.
The third location is at (30mm) and the forth at (40mm) from the sharp edge within insulated part.
The best values of hardness for the insulated specimen with graphite are (65,64HRC) within the un insulated part and (47,48 HRC) within the insulated part.
For the specimen with ceramic insulation the hardness values are (65,64 HRC) within the un insulated part and (51,52 HRC) within the insulated part.
The results of this work was applied on the active parts of some press working sheet metal dies, produced in central tool room plant/Nasser state company, it has been shown that the life and fracture strength of these parts (punch, die and stripper) were increased and improved.
American Psychological Association (APA)
الونداوي، نيفين جمال. 2009. تأثير المعاملة الحرارية الجزئية على الخواص الميكانيكية لصلب العدة عالي الكربون المستخدم في صناعة الأجزاء الفعالة لقوالب القطع على البارد. مجلة الهندسة والتكنولوجيا،مج. 27، ع. 05، ص ص. 180-189.
https://search.emarefa.net/detail/BIM-49700
Modern Language Association (MLA)
الونداوي، نيفين جمال. تأثير المعاملة الحرارية الجزئية على الخواص الميكانيكية لصلب العدة عالي الكربون المستخدم في صناعة الأجزاء الفعالة لقوالب القطع على البارد. مجلة الهندسة والتكنولوجيا مج. 27، ع. 05 (2009)، ص ص. 180-189.
https://search.emarefa.net/detail/BIM-49700
American Medical Association (AMA)
الونداوي، نيفين جمال. تأثير المعاملة الحرارية الجزئية على الخواص الميكانيكية لصلب العدة عالي الكربون المستخدم في صناعة الأجزاء الفعالة لقوالب القطع على البارد. مجلة الهندسة والتكنولوجيا. 2009. مج. 27، ع. 05، ص ص. 180-189.