دراسة خصائص متراكبات سميكات الصوديوم كحاجز وقائي يفصل بين بطانة أبراج التصفية النفطية و الأبخرة الكيميائية للنفط الخام

Abstract EN

The study of surface hardness, wear resistance, adhesion strength, electrochemical corrosion resistance and thermal conductivity of coatings composed from sodium silicate was prepared using graphite micro-size particles and carbon nano particles as fillers respectively of concentration of (1-5%), for the purpose of covering and protecting the oil distillation towers.

The results showed that the sodium silicate coating reinforced with carbon nano-powder has higher resistance to stitches, mechanical wear, adhesive and thermal conductivity than graphite/sodium silicate composite especially when the ratio 5% and 1%, the electrochemical corrosion test confirmed that the coating process of stainless steel 304 lead to increasing the corrosion resistance, where the reinforcing of sodium silicate lead to a significant improvement in the corrosion resistance, the corrosion resistance behavior change depending on the type of reinforcement material, this is consistent with the field test results.