تأثير المعاملات الحرارية المختلفة على السلوك التاكلي للهايدروكسي أبتايت المطلي على سبيكة Ti-6Al-4V بطريقة الترسيب بهجرة الدقائق المشحونة و طريقة التغطيس

Abstract EN

In this research, the study of thermal treating by laser, plasma glow discharge and tubular furnace on Ti-6Al-4V alloy coated with hydroxyapatite by methods of dip coating and electrophoretic deposition .A group of samples was coated by dip coating and another group was coated by electrophoretic deposition.

The first group was treated by pulse laser 10 (mJ) as energy for samples from both coating with uniform distributed pulses on every single sample surface, The second thermal treating was made by plasma glow discharge in a locally made system with argon atmosphere, 600 Volt , and 6 cm distance between the electrodes, The third treating was made by tubular furnace in air atmosphere and 400 °C for 1 hour duration.

Then the samples were tested by optical microscope, XRD, SEM, and the corrosion characteristic with open circuit potential (OCP) and polarization curve (Tafel), The results showed that the samples tr eated by tubular furnace were the best where the corrosion rate was reduced to 3.567×10-4 mm/y for the dip coated samples and 7.221×10-4 mm/y for the electrophoretic deposited samples compared with 9.396×10-3mm/y for uncoated sample.