دراسة الخصائص الكهربائية و المغناطسية و الامتصاصية لفيرايت السبينل نوع Ca1-xNixFe2O4 باستخدام المحلل الشبكي

Abstract EN

In this work, the spinal ferrite Ca1-xNixFe2O4 has been prepared where X  (0,0.2,0.4,0.6,0.8) , used.

as radar absorbing materials (RAM).

Conventional ceramic techniques method was used to prepare these materials at X band microwaves with the range of frequencies (8-12) GHz.

The absorption for microwaves was examined by the utilized the network analyzer.

The relationship between reflectivity, absorption and attenuation coefficient were plotted as a function of frequency, and sintered at a temperature C  1100 .

The results showed the emergence of several resonance peaks at X  band , samples showed high Absorbency in contrast low reflectivity and high values of attenuation coefficient at the same frequencies, this is due to domain rotation as well domain wall motion of the ferrite.

The values of the real and imaginary parts of relative magnetic Permeability and relative electric permittivity were measure for all samples.

The results revealed the apparent resonance peaks at same frequencies that apparent at absorption and reflectivity curves of the same samples.

X-ray diffraction tests were made for one sample and result showed the structure of the sample is polycrystalline