Synthesis of Highly Emissive CdSe Quantum Dots by Aqueous Precipitation Method

الملخص EN

CdSe quantum dots (QDs) with high quantum yield (QY) up to 76.57% are synthesized using the aqueous precipitation method.

With the control of SeSO32- concentration in Se precursor, the nucleation speed and concentration of CdSe QDs are increased.

The mass of obtained Cd2+ and Se2+ in nanocrystal is measured by inductively coupled plasma atomic emission spectrometry (ICP-AES).

XRD and HRTEM are used to identify the crystal phase and morphology of the products which are pure CdSe crystals in the cubic zinc blende phase and uniformly dispersed in the solution with the size between 2 nm and 2.3 nm.

Results demonstrate that the emission wavelength of CdSe QDs is 500 nm~560 nm along with the increased temperature 50°C~90°C and prolonged time 5 min~25 min.