Fabrication and Enhanced Thermoelectric Properties of Alumina Nanoparticle-Dispersed Bi0.5Sb1.5Te3 Matrix Composites

الملخص EN

Alumina nanoparticle-dispersed bismuth-antimony-tellurium matrix (Al2O3/BST) composite powders were fabricated by using ball milling process of alumina nanoparticle about 10 nm and p-type bismuth telluride nanopowders prepared from the mechanochemical process (MCP).

The fabricated Al2O3/BST composite powders were a few hundreds of nanometer in size, with a clear Bi0.5Sb1.5Te3 phase.

The composite powders were consolidated into p-type bulk composite by spark plasma sintering process.

High-resolution TEM images reveal that alumina nanoparticles were dispersed among the grain boundary or in the matrix grain.

The sintered 0.3 vol.% Al2O3/BST composite exhibited significantly improved power factor and reduced thermal conductivity in the temperature ranging from 293 to 473 K compared to those of pure BST.

From these results, the highly increased ZT value of 1.5 was obtained from 0.3 vol.% Al2O3/BST composite at 323 K.