Effect of Different Seed Solutions on the Morphology and Electrooptical Properties of ZnO Nanorods

الملخص EN

The morphology and electrooptical properties of ZnO nanorods synthesized on monoethanolamine-based seed layer and KOH-based seed layer were compared.

The seed solutions were prepared in monoethanolamine in 2-methoxyethanol and potassium hydroxide in methanol, respectively.

Zinc acetate dihydrate was as a common precursor in both solutions.

The nanorod-ZnOs were synthesized via the spin coating of two different seed solutions on silicon substrates followed by their hydrothermal growth.

The scanning electron microscopy (SEM), X-ray diffraction (XRD), photoluminescence (PL), and Raman studies revealed that the ZnO nanorods obtained from monoethanolamine-based seed layer had fewer defects, better crystals, and better alignment than those realized via KOH-based seed layer.

However, the current-voltage (I-V) characteristics demonstrated better conductivity of the ZnO nanorods obtained via KOH-based seed layer.

The current measured in forward bias was 4 mA and 40 μA for ZnO-nanorods grown on KOH-based seed layer and monoethanolamine-based with the turn on voltage of approximately 1.5 V and 2.5 V, respectively, showing the feasibility of using both structures in optoelectric devices.