The Role of Nanostructured Al2O3 Layer in Reduction of Hot Corrosion Products in Normal YSZ Layer
المؤلفون المشاركون
Noordin, M. Y.
Sakhawat Hussain, Mohammad
Azizi Mat Yajid, Muhamad
Daroonparvar, Mohammadreza
المصدر
العدد
المجلد 2013، العدد 2013 (31 ديسمبر/كانون الأول 2013)، ص ص. 1-11، 11ص.
الناشر
Hindawi Publishing Corporation
تاريخ النشر
2013-03-10
دولة النشر
مصر
عدد الصفحات
11
التخصصات الرئيسية
الملخص EN
YVO4 crystals and monoclinic ZrO2 are known as hot corrosion products that can considerably reduce the lifetime of thermal barrier coatings during service.
The hot corrosion resistance of two types of air plasma sprayed thermal barrier coating systems was investigated: an Inconel 738/NiCrAlY/YSZ (yttria-stabilized zirconia) and an Inconel 738/NiCrAlY/YSZ/nano-Al2O3 as an outer layer.
Hot corrosion test was accomplished on the outer surface of coatings in molten salts (45% Na2SO4 + 55% V2O5) at 1000°C for 52 hour.
It was found that nanostructured alumina as outer layer of YSZ/nano-Al2O3 coating had significantly reduced the infiltration of molten salts into the YSZ layer and resulted in lower reaction of fused corrosive salts with YSZ, as the hot corrosion products had been substantially decreased in YSZ/nano-Al2O3 coating in comparison with normal YSZ coating after hot corrosion process.
نمط استشهاد جمعية علماء النفس الأمريكية (APA)
Daroonparvar, Mohammadreza& Azizi Mat Yajid, Muhamad& Noordin, M. Y.& Sakhawat Hussain, Mohammad. 2013. The Role of Nanostructured Al2O3 Layer in Reduction of Hot Corrosion Products in Normal YSZ Layer. Journal of Nanomaterials،Vol. 2013, no. 2013, pp.1-11.
https://search.emarefa.net/detail/BIM-1031326
نمط استشهاد الجمعية الأمريكية للغات الحديثة (MLA)
Daroonparvar, Mohammadreza…[et al.]. The Role of Nanostructured Al2O3 Layer in Reduction of Hot Corrosion Products in Normal YSZ Layer. Journal of Nanomaterials No. 2013 (2013), pp.1-11.
https://search.emarefa.net/detail/BIM-1031326
نمط استشهاد الجمعية الطبية الأمريكية (AMA)
Daroonparvar, Mohammadreza& Azizi Mat Yajid, Muhamad& Noordin, M. Y.& Sakhawat Hussain, Mohammad. The Role of Nanostructured Al2O3 Layer in Reduction of Hot Corrosion Products in Normal YSZ Layer. Journal of Nanomaterials. 2013. Vol. 2013, no. 2013, pp.1-11.
https://search.emarefa.net/detail/BIM-1031326
نوع البيانات
مقالات
لغة النص
الإنجليزية
الملاحظات
Includes bibliographical references
رقم السجل
BIM-1031326
قاعدة معامل التأثير والاستشهادات المرجعية العربي "ارسيف Arcif"
أضخم قاعدة بيانات عربية للاستشهادات المرجعية للمجلات العلمية المحكمة الصادرة في العالم العربي
![](/images/ebook-kashef.png)
تقوم هذه الخدمة بالتحقق من التشابه أو الانتحال في الأبحاث والمقالات العلمية والأطروحات الجامعية والكتب والأبحاث باللغة العربية، وتحديد درجة التشابه أو أصالة الأعمال البحثية وحماية ملكيتها الفكرية. تعرف اكثر
![](/images/kashef-image.png)