High Temperature Corrosion of Inconel 600 in NaCl-KCl Molten Salts
المؤلفون المشاركون
Gonzalez-Rodriguez, J. G.
Porcayo-Calderon, J.
Salinas-Solano, G.
Ascencio-Gutierrez, J. A.
Martinez-Gomez, L.
Salinas-Bravo, V. M.
المصدر
Advances in Materials Science and Engineering
العدد
المجلد 2014، العدد 2014 (31 ديسمبر/كانون الأول 2014)، ص ص. 1-8، 8ص.
الناشر
Hindawi Publishing Corporation
تاريخ النشر
2014-12-30
دولة النشر
مصر
عدد الصفحات
8
الملخص EN
In this work the corrosion resistance of a high content nickel alloy, Inconel 600, was investigated in mixed NaCl-KCl salts at 700, 800, and 900°C for 100 hours in static air.
Investigation was carried out using electrochemical techniques such as polarization curves, rest potential measurements, linear polarization resistance, and electrochemical impedance spectroscopy.
Corroded specimens were analyzed by scanning electron microscopy (SEM) and energy-dispersive X-ray spectroscopy (EDS).
Electrochemical measurements showed an increased degradation rate of Inconel 600 with increasing test temperature.
SEM and EDS analysis show that the damage experienced by Inconel 600 is greater than that determined by electrochemical measurements.
This damage was identified as internal corrosion due to the reaction of Cl2 with the alloying elements (Cr and Fe); however, at 900°C the internal damage was minor and it was associated with the nickel content in the alloy.
نمط استشهاد جمعية علماء النفس الأمريكية (APA)
Salinas-Solano, G.& Porcayo-Calderon, J.& Gonzalez-Rodriguez, J. G.& Salinas-Bravo, V. M.& Ascencio-Gutierrez, J. A.& Martinez-Gomez, L.. 2014. High Temperature Corrosion of Inconel 600 in NaCl-KCl Molten Salts. Advances in Materials Science and Engineering،Vol. 2014, no. 2014, pp.1-8.
https://search.emarefa.net/detail/BIM-1034297
نمط استشهاد الجمعية الأمريكية للغات الحديثة (MLA)
Salinas-Solano, G.…[et al.]. High Temperature Corrosion of Inconel 600 in NaCl-KCl Molten Salts. Advances in Materials Science and Engineering No. 2014 (2014), pp.1-8.
https://search.emarefa.net/detail/BIM-1034297
نمط استشهاد الجمعية الطبية الأمريكية (AMA)
Salinas-Solano, G.& Porcayo-Calderon, J.& Gonzalez-Rodriguez, J. G.& Salinas-Bravo, V. M.& Ascencio-Gutierrez, J. A.& Martinez-Gomez, L.. High Temperature Corrosion of Inconel 600 in NaCl-KCl Molten Salts. Advances in Materials Science and Engineering. 2014. Vol. 2014, no. 2014, pp.1-8.
https://search.emarefa.net/detail/BIM-1034297
نوع البيانات
مقالات
لغة النص
الإنجليزية
الملاحظات
Includes bibliographical references
رقم السجل
BIM-1034297
قاعدة معامل التأثير والاستشهادات المرجعية العربي "ارسيف Arcif"
أضخم قاعدة بيانات عربية للاستشهادات المرجعية للمجلات العلمية المحكمة الصادرة في العالم العربي
تقوم هذه الخدمة بالتحقق من التشابه أو الانتحال في الأبحاث والمقالات العلمية والأطروحات الجامعية والكتب والأبحاث باللغة العربية، وتحديد درجة التشابه أو أصالة الأعمال البحثية وحماية ملكيتها الفكرية. تعرف اكثر