Morphological Investigation of Calcium Carbonate during Ammonification-Carbonization Process of Low Concentration Calcium Solution
المؤلفون المشاركون
Cheng, Huaigang
Zhang, Xiaoxi
Song, Huiping
المصدر
العدد
المجلد 2014، العدد 2014 (31 ديسمبر/كانون الأول 2014)، ص ص. 1-7، 7ص.
الناشر
Hindawi Publishing Corporation
تاريخ النشر
2014-09-02
دولة النشر
مصر
عدد الصفحات
7
التخصصات الرئيسية
الملخص EN
Ultrafine calcium carbonate is a widely used cheap additive.
The research is conducted in low degree supersaturation solution in order to study the polymorphic phases’ change and its factors of the calcium carbonate precipitate in the ammonification-carbonization process of the solution with calcium.
Fine particles of calcium carbonate are made in the solution containing 0.015 mol/L of Ca2+.
Over 98% of the calcium carbonate precipitate without ammonification resembles the morphology of calcite, while the introduction of ammonia can benefit the formation of vaterite.
It was inferred that the main cause should be serious partial oversaturation or steric effects.
Ammonia also helps to form the twin spherical calcium carbonate.
However, particles formed in the process of ammonification-carbonization in solution with low concentration degree of calcium are not even with a scale of the particle diameter from 5 to 12 μm.
Inorganic salts, alcohol, or organic acid salts have significant controlling effect on the particle diameter of calcium carbonate and can help to decrease the particle diameter to about 3 μm.
Anionic surfactants can prevent the conglobation of calcium carbonate particles and shrink its diameter to 500 nm–1 μm.
نمط استشهاد جمعية علماء النفس الأمريكية (APA)
Cheng, Huaigang& Zhang, Xiaoxi& Song, Huiping. 2014. Morphological Investigation of Calcium Carbonate during Ammonification-Carbonization Process of Low Concentration Calcium Solution. Journal of Nanomaterials،Vol. 2014, no. 2014, pp.1-7.
https://search.emarefa.net/detail/BIM-1041598
نمط استشهاد الجمعية الأمريكية للغات الحديثة (MLA)
Cheng, Huaigang…[et al.]. Morphological Investigation of Calcium Carbonate during Ammonification-Carbonization Process of Low Concentration Calcium Solution. Journal of Nanomaterials No. 2014 (2014), pp.1-7.
https://search.emarefa.net/detail/BIM-1041598
نمط استشهاد الجمعية الطبية الأمريكية (AMA)
Cheng, Huaigang& Zhang, Xiaoxi& Song, Huiping. Morphological Investigation of Calcium Carbonate during Ammonification-Carbonization Process of Low Concentration Calcium Solution. Journal of Nanomaterials. 2014. Vol. 2014, no. 2014, pp.1-7.
https://search.emarefa.net/detail/BIM-1041598
نوع البيانات
مقالات
لغة النص
الإنجليزية
الملاحظات
Includes bibliographical references
رقم السجل
BIM-1041598
قاعدة معامل التأثير والاستشهادات المرجعية العربي "ارسيف Arcif"
أضخم قاعدة بيانات عربية للاستشهادات المرجعية للمجلات العلمية المحكمة الصادرة في العالم العربي
تقوم هذه الخدمة بالتحقق من التشابه أو الانتحال في الأبحاث والمقالات العلمية والأطروحات الجامعية والكتب والأبحاث باللغة العربية، وتحديد درجة التشابه أو أصالة الأعمال البحثية وحماية ملكيتها الفكرية. تعرف اكثر