Mineral Phases and Release Behaviors of As in the Process of Sintering Residues Containing As at High Temperature
المؤلفون المشاركون
Zhang, Fengsong
Xing-run, Wang
Yan-xia, Zhang
المصدر
العدد
المجلد 2014، العدد 2014 (31 ديسمبر/كانون الأول 2014)، ص ص. 1-8، 8ص.
الناشر
Hindawi Publishing Corporation
تاريخ النشر
2014-03-01
دولة النشر
مصر
عدد الصفحات
8
التخصصات الرئيسية
الطب البشري
تكنولوجيا المعلومات وعلم الحاسوب
الملخص EN
To investigate the effect of sintering temperature and sintering time on arsenic volatility and arsenic leaching in the sinter, we carried out experimental works and studied the structural changes of mineral phases and microstructure observation of the sinter at different sintering temperatures.
Raw materials were shaped under the pressure of 10 MPa and sintered at 1000~1350°C for 45 min with air flow rate of 2000 mL/min.
The results showed that different sintering temperatures and different sintering times had little impact on the volatilization of arsenic, and the arsenic fixed rate remained above 90%; however, both factors greatly influenced the leaching concentration of arsenic.
Considering the product’s environmental safety, the best sintering temperature was 1200°C and the best sintering time was 45 min.
When sintering temperature was lower than 1000°C, FeAsS was oxidized into calcium, aluminum, and iron arsenide, mainly Ca3(AsO4)2 and AlAsO4, and the arsenic leaching was high.
When it increased to 1200°C, arsenic was surrounded by a glass matrix and became chemically bonded inside the matrix, which lead to significantly lower arsenic leaching.
نمط استشهاد جمعية علماء النفس الأمريكية (APA)
Xing-run, Wang& Zhang, Fengsong& Yan-xia, Zhang. 2014. Mineral Phases and Release Behaviors of As in the Process of Sintering Residues Containing As at High Temperature. The Scientific World Journal،Vol. 2014, no. 2014, pp.1-8.
https://search.emarefa.net/detail/BIM-1048946
نمط استشهاد الجمعية الأمريكية للغات الحديثة (MLA)
Xing-run, Wang…[et al.]. Mineral Phases and Release Behaviors of As in the Process of Sintering Residues Containing As at High Temperature. The Scientific World Journal No. 2014 (2014), pp.1-8.
https://search.emarefa.net/detail/BIM-1048946
نمط استشهاد الجمعية الطبية الأمريكية (AMA)
Xing-run, Wang& Zhang, Fengsong& Yan-xia, Zhang. Mineral Phases and Release Behaviors of As in the Process of Sintering Residues Containing As at High Temperature. The Scientific World Journal. 2014. Vol. 2014, no. 2014, pp.1-8.
https://search.emarefa.net/detail/BIM-1048946
نوع البيانات
مقالات
لغة النص
الإنجليزية
الملاحظات
Includes bibliographical references
رقم السجل
BIM-1048946
قاعدة معامل التأثير والاستشهادات المرجعية العربي "ارسيف Arcif"
أضخم قاعدة بيانات عربية للاستشهادات المرجعية للمجلات العلمية المحكمة الصادرة في العالم العربي
![](/images/ebook-kashef.png)
تقوم هذه الخدمة بالتحقق من التشابه أو الانتحال في الأبحاث والمقالات العلمية والأطروحات الجامعية والكتب والأبحاث باللغة العربية، وتحديد درجة التشابه أو أصالة الأعمال البحثية وحماية ملكيتها الفكرية. تعرف اكثر
![](/images/kashef-image.png)