Chemical Changes Associated with Increased Acid Resistance of Er:YAG Laser Irradiated Enamel

الملخص EN

Background.

An increase in the acid resistance of dental enamel, as well as morphological and structural changes produced by Er:YAG laser irradiation, has been reported.

Purpose.

To evaluate the chemical changes associated with acid resistance of enamel treated with Er:YAG laser.

Methods.

Forty-eight enamel samples were divided into 4 groups ( n = 12 ).

Group I (control); Groups II, III, and IV were irradiated with Er:YAG at 100 mJ (12.7 J/cm2), 200 mJ (25.5 J/cm2), and 300 mJ (38.2 J/cm2), respectively.

Results.

There were significant differences in composition of irradiated groups (with the exception of chlorine) and in the amount of calcium released.

Conclusions.

Chemical changes associated with an increase in acid resistance of enamel treated with Er:YAG laser showed a clear postirradiation pattern characterized by a decrease in C at.% and an increase in O, P, and Ca at.% and no changes in Cl at.%.

An increased Ca/P ratio after Er:YAG laser irradiation was associated with the use of higher laser energy densities.

Chemical changes produced by acid dissolution showed a similar trend among experimental groups.

Stable or increased Ca/P ratio after acid dissolution was observed in the irradiated groups, with reduction of Ca released into the acid solution.