Microstructure and Mechanical Property of Hot-Pressed Al2O3-Ni-P Composites Using Ni-P-Coated Al2O3 Powders
المؤلفون المشاركون
المصدر
Advances in Materials Science and Engineering
العدد
المجلد 2015، العدد 2015 (31 ديسمبر/كانون الأول 2015)، ص ص. 1-6، 6ص.
الناشر
Hindawi Publishing Corporation
تاريخ النشر
2015-12-29
دولة النشر
مصر
عدد الصفحات
6
الملخص EN
Al2O3-Ni-P composite powders with Ni-P contents of 10.9, 14.4, and 20.4 wt.% were synthesized via the Ni-P electroless deposition process.
The as-received Al2O3-Ni-P composite powders were composed of Ni-P particles and Ni-P coating layer.
Some Ni-P particles randomly adhered to the Al2O3 powders, and their particle diameter ranged from 5 nm to 20 nm.
The thin Ni-P layer had about 5 nm thick amorphous structure and directly bonded with Al2O3 powders.
Using the Ni-P-coated Al2O3 powders, a dense Al2O3-Ni-P composite can be successfully obtained using the hot press process at 1,350°C for 1 hour in an Ar atmosphere under an applied pressure of 30 MPa.
The hot-pressed Al2O3-15 wt.% Ni-P composite showed excellent material properties.
Its relative density, Vickers hardness, and fracture toughness were comparatively high: about 99.1%, 2,360 Hv, and 6 MPa·m1/2, respectively.
The fracture surface of the hot-pressed Al2O3-Ni-P composite showed a semiductile mode due to the mixed intergranular and transgranular fracture mode.
In particular, the fracture toughness of the hot-pressed Al2O3-15 wt.% Ni-P composite was strongly enhanced by the combined action of the crack branching and the crack deflection.
نمط استشهاد جمعية علماء النفس الأمريكية (APA)
Kim, Hyeong-Chul& Han, Jae-Kil. 2015. Microstructure and Mechanical Property of Hot-Pressed Al2O3-Ni-P Composites Using Ni-P-Coated Al2O3 Powders. Advances in Materials Science and Engineering،Vol. 2015, no. 2015, pp.1-6.
https://search.emarefa.net/detail/BIM-1053079
نمط استشهاد الجمعية الأمريكية للغات الحديثة (MLA)
Kim, Hyeong-Chul& Han, Jae-Kil. Microstructure and Mechanical Property of Hot-Pressed Al2O3-Ni-P Composites Using Ni-P-Coated Al2O3 Powders. Advances in Materials Science and Engineering No. 2015 (2015), pp.1-6.
https://search.emarefa.net/detail/BIM-1053079
نمط استشهاد الجمعية الطبية الأمريكية (AMA)
Kim, Hyeong-Chul& Han, Jae-Kil. Microstructure and Mechanical Property of Hot-Pressed Al2O3-Ni-P Composites Using Ni-P-Coated Al2O3 Powders. Advances in Materials Science and Engineering. 2015. Vol. 2015, no. 2015, pp.1-6.
https://search.emarefa.net/detail/BIM-1053079
نوع البيانات
مقالات
لغة النص
الإنجليزية
الملاحظات
Includes bibliographical references
رقم السجل
BIM-1053079
قاعدة معامل التأثير والاستشهادات المرجعية العربي "ارسيف Arcif"
أضخم قاعدة بيانات عربية للاستشهادات المرجعية للمجلات العلمية المحكمة الصادرة في العالم العربي
تقوم هذه الخدمة بالتحقق من التشابه أو الانتحال في الأبحاث والمقالات العلمية والأطروحات الجامعية والكتب والأبحاث باللغة العربية، وتحديد درجة التشابه أو أصالة الأعمال البحثية وحماية ملكيتها الفكرية. تعرف اكثر