Microstructures and Toughening of TiC-TiB2 Ceramic Composites with Cr-Based Alloy Phase Prepared by Combustion Synthesis in High-Gravity Field

الملخص EN

Micro-nanocrystalline microstructures which are characterized by TiB2 platelets of the average thickness close to or smaller than 1 μm can be achieved in nearly full-density solidified TiC-TiB2 ceramic composites with Cr-based alloy phases by combustion synthesis in ultra-high gravity field of 2500 g.

The filler phases in ceramic composites are actually Cr-based alloy with a little solidified solution of Ni atoms and Al atoms.

The hardness, flexural strength, and fracture toughness of the materials are 18.5 ± 1.5 GPa, 650 ± 35 MPa, and 16.5 ± 1.5 MPa⋅m0.5, respectively.

The improved fracture toughness of TiC-TiB2 ceramic composites results from crack deflection, crack bridging, and pull-out by a large number of fine TiB2 platelets and plastic deformation with some Cr-based alloy phases.