The Effect of Welding Residual Stress for Making Artificial Stress Corrosion Crack in the STS 304 Pipe
المؤلفون المشاركون
Kim, Jae-Seong
Lee, Bo-Young
Hwang, Woong-Gi
Kang, Sung-Sik
المصدر
Advances in Materials Science and Engineering
العدد
المجلد 2015، العدد 2015 (31 ديسمبر/كانون الأول 2015)، ص ص. 1-7، 7ص.
الناشر
Hindawi Publishing Corporation
تاريخ النشر
2015-03-02
دولة النشر
مصر
عدد الصفحات
7
الملخص EN
The stress corrosion crack is one of the fracture phenomena for the major structure components in nuclear power plant.
During the operation of a power plant, stress corrosion cracks are initiated and grown especially in dissimilar weldment of primary loop components.
In particular, stress corrosion crack usually occurs when the following three factors exist at the same time: susceptible material, corrosive environment, and tensile stress (residual stress included).
Thus, residual stress becomes a critical factor for stress corrosion crack when it is difficult to improve the material corrosivity of the components and their environment under operating conditions.
In this study, stress corrosion cracks were artificially produced on STS 304 pipe itself by control of welding residual stress.
We used the instrumented indentation technique and 3D FEM analysis (using ANSYS 12) to evaluate the residual stress values in the GTAW area.
We used the custom-made device for fabricating the stress corrosion crack in the inner STS 304 pipe wall.
As the result of both FEM analysis and experiment, the stress corrosion crack was quickly generated and could be reproduced, and it could be controlled by welding residual stress.
نمط استشهاد جمعية علماء النفس الأمريكية (APA)
Kim, Jae-Seong& Lee, Bo-Young& Hwang, Woong-Gi& Kang, Sung-Sik. 2015. The Effect of Welding Residual Stress for Making Artificial Stress Corrosion Crack in the STS 304 Pipe. Advances in Materials Science and Engineering،Vol. 2015, no. 2015, pp.1-7.
https://search.emarefa.net/detail/BIM-1053728
نمط استشهاد الجمعية الأمريكية للغات الحديثة (MLA)
Kim, Jae-Seong…[et al.]. The Effect of Welding Residual Stress for Making Artificial Stress Corrosion Crack in the STS 304 Pipe. Advances in Materials Science and Engineering No. 2015 (2015), pp.1-7.
https://search.emarefa.net/detail/BIM-1053728
نمط استشهاد الجمعية الطبية الأمريكية (AMA)
Kim, Jae-Seong& Lee, Bo-Young& Hwang, Woong-Gi& Kang, Sung-Sik. The Effect of Welding Residual Stress for Making Artificial Stress Corrosion Crack in the STS 304 Pipe. Advances in Materials Science and Engineering. 2015. Vol. 2015, no. 2015, pp.1-7.
https://search.emarefa.net/detail/BIM-1053728
نوع البيانات
مقالات
لغة النص
الإنجليزية
الملاحظات
Includes bibliographical references
رقم السجل
BIM-1053728
قاعدة معامل التأثير والاستشهادات المرجعية العربي "ارسيف Arcif"
أضخم قاعدة بيانات عربية للاستشهادات المرجعية للمجلات العلمية المحكمة الصادرة في العالم العربي
![](/images/ebook-kashef.png)
تقوم هذه الخدمة بالتحقق من التشابه أو الانتحال في الأبحاث والمقالات العلمية والأطروحات الجامعية والكتب والأبحاث باللغة العربية، وتحديد درجة التشابه أو أصالة الأعمال البحثية وحماية ملكيتها الفكرية. تعرف اكثر
![](/images/kashef-image.png)