Microstructure Control of Columnar-Grained Silicon Substrate Solidified from Silicon Melts Using Gas Pressure

الملخص EN

A silicon substrate with the dimensions of 100 × 140 × 0.3 mm was grown directly from liquid silicon with gas pressure.

The silicon melt in the sealed melting part was injected into the growth part at applied pressure of 780–850 Torr.

The solidified silicon substrate was then transferred by the pull of the cooled dummy bar.

A desirable structure with a liquid-solid interface perpendicular to the pulling direction was formed when the mold temperature in the solidification zone of the growth part was much higher than that of the dummy bar, as this technique should be able to overcome thermal loss through the molds and the limited heat flux derived from the very narrow contact area between the silicon melt and the dummy bar.

In addition, because the metallic impurities and expansion of volume during solidification are preferably moved to a liquid phase, a high-quality silicon substrate, without defects such as cracks and impurities in the substrate, could be manufactured in the interface structure.

The present study reports the experimental findings on a new and direct growth system for obtaining silicon substrates characterized by high quality and productivity, as a candidate for alternate routes for the fabrication of silicon substrates.