The Photoluminescence Behaviors of a Novel Reddish Orange Emitting Phosphor CaIn2O4:Sm3+ Codoped with Zn2+ or Al3+ Ions

الملخص EN

A novel reddish orange phosphor CaIn2O4:Sm3+ codoped with Zn2+ or Al3+ ions was prepared by solid state reaction and their luminescence properties were investigated under near ultraviolet excitation.

The strategy of Zn2+ or Al3+ ions codoping was used with the aim to improve the luminescence properties of CaIn2O4:Sm3+, but the concrete effects of the two ions is different.

The introduction of Zn2+ ions can produce Zn In ' defects that favor charge balance in CaIn2O4:Sm3+ to facilitate its photoluminescence.

The effect of Al3+ ions codoping can effectively transfer energy from charge-transfer absorption band to characteristic transition of Sm3+ ions, utilizing more energy from host absorption for the photoluminescence of Sm3+ ions.

Based on these mechanisms, the luminescence intensity of CaIn2O4:0.6%Sm3+ was enhanced to 1.59 times and 1.51 times when codoping amount of Zn2+ and Al3+ ions reached 0.6%.

However, the chromaticity coordinates of CaIn2O4:0.6%Sm3+ almost did not have any changes after Zn2+ ions or Al3+ ions codoping; those are still located at reddish orange region.

The excellent luminescence properties of CaIn2O4:0.6%Sm3+,0.6%Zn2+ and CaIn2O4:0.6%Sm3+,0.6%Al3+ demonstrate that they both have potential application value as new-style reddish orange phosphors on light-emitting diode.