Applicability of the Modified Ritchie-Knott-Rice Failure Criterion to Examine the Feasibility of Miniaturized Charpy Type SE(B)‎ Specimens

الملخص EN

This paper examined whether the modified Ritchie-Knott-Rice (RKR) failure criterion can be applied to examine the feasibility of miniaturized Charpy type SE(B) specimens of thickness-to-width ratio B/W=1.

The modified RKR failure criterion considered in this paper is the (4δt,σ22c) criterion which predicts the onset of cleavage fracture when the midplane crack-opening stress measured at a distance equal to four times the crack-tip opening displacement, denoted as σ22d, exceeds a critical stress σ22c.

Specimens with B values of 25, 10, 3, and 2 mm (denoted as 25t, 10t, 3t, and 2t specimens, resp.) manufactured with 0.55% carbon steel were tested at 20°C.

The results showed that the modified RKR criterion could appropriately predict the occurrence of cleavage fracture accompanied by negligibly small stable crack extension (denoted as KJc fracture) naturally for the 25t and 10t specimens.

The modified RKR criterion could also predict that KJc fracture does not occur for the 2t specimen.

The σ22c obtained from specimens for the 25t and 10t specimens exhibited only a small difference, indicating that the Jc obtained from the 10t specimens can be used to predict the Jc that will be obtained with the 25t specimens.