Simulated Experiment Study of Factors Influencing the Hydration Activity of f-CaO in Basic Oxygen Furnace Slag

الملخص EN

The compositions and formation process of f-CaO in BOF slag were revealed and simulated to understand its expansion rules and why its hydration activity is low.

BSE showed the compositions of f-CaO, which included calcium iron phase and calcium iron manganese phase, were diverse.

The hydration activity sequence was Ca2Fe2O5 and Ca3Fe1.5Mn1.5O8 in tricomponent f-CaO < CaO in tricomponent f-CaO < monocomponent f-CaO; only Ca2Fe2O5 and Ca3Fe1.5Mn1.5O8 were hard to hydrate, and the volume expansion rates of the tricomponent f-CaO varied with different compositions.

Inductively, in BOF slag, the hydration activity sequence was solid solutions CaO-FeOx and CaO-FeOx-MnOy in tricomponent f-CaO < CaO in tricomponent f-CaO < monocomponent f-CaO; the volume expansion rates of tricomponent f-CaO changed with different compositions, and CaO-FeOx and CaO-FeOx-MnOy were difficult to hydrate.

The reason why solid solutions CaO-FeOx and CaO-FeOx-MnOy were hard to hydrate was that their hydration reaction driving force, which is the absolute value of standard molar reaction Gibbs functions, decreased.