The Influence of Irradiation Time and Layer Thickness on Elution of Triethylene Glycol Dimethacrylate from SDR® Bulk-Fill Composite

الملخص EN

Objective.

This study aimed to evaluate triethylene glycol dimethacrylate (TEGDMA) elution from SDR bulk-fill composite.

Methods.

Three groups of samples were prepared, including samples polymerized in a 4 mm layer for 20 s, in a 4 mm layer for 40 s, and in a 2 mm layer for 20 s.

Elution of TEGDMA into 100% ethanol, a 75% ethanol/water solution, and distilled water was studied.

The TEGDMA concentration was measured using HPLC.

Results.

The TEGDMA concentration decreased in the following order: 100% ethanol > 75% ethanol > distilled water.

Doubling the energy delivered to the 4 mm thick sample caused decrease ( p < 0.05 ) in TEGDMA elution to distilled water.

In ethanol solutions, the energy increase had no influence on TEGDMA elution.

Decreasing the sample thickness resulted in decrease ( p < 0.05 ) in TEGDMA elution for all the solutions.

Conclusions.

The concentration of eluted TEGDMA and the elution time were both strongly affected by the hydrophobicity of the solvent.

Doubling the energy delivered to the 4 mm thick sample did not decrease the elution of TEGDMA but did decrease the amount of the monomer available to less aggressive solvents.

Elution of TEGDMA was also correlated with the exposed sample surface area.

Clinical Relevance.

Decreasing the SDR layer thickness decreases TEGDMA elution.