Service Life Prediction of Precast Concrete Structures Exposed to Chloride Environment
المؤلفون المشاركون
Zhang, Dawei
Zeng, Yu
Fang, Mingshan
Jin, Weiliang
المصدر
العدد
المجلد 2019، العدد 2019 (31 ديسمبر/كانون الأول 2019)، ص ص. 1-14، 14ص.
الناشر
Hindawi Publishing Corporation
تاريخ النشر
2019-05-02
دولة النشر
مصر
عدد الصفحات
14
التخصصات الرئيسية
الملخص EN
Chloride-induced corrosion is widely accepted as one of the primary causes of premature deterioration for concrete structures in marine or deicing salt environment.
For precast concrete (PC) structures, such durability problems may even be severer because defects in joint areas, e.g., cracks caused by grout shrinkage and improper construction, can accelerate chloride ion transportation process and may cause the interface shear failure when subjected to seismic load.
By applying the path probability model (PPM) and reliability theory, a probabilistic framework was proposed to predict three limit states of PC structures, including corrosion initiation, serviceability limit state, and ultimate limit state.
Using Monte Carlo simulation, a beam-to-column joint was further analyzed to illustrate the differences between PC structures and those cast in situ.
The analysis indicates that corrosion initiation and serviceability limit state are sensitive to chloride diffusivity at connection area, and the higher pitting factor can significantly influence the bearing capacities of PC structures.
نمط استشهاد جمعية علماء النفس الأمريكية (APA)
Zhang, Dawei& Zeng, Yu& Fang, Mingshan& Jin, Weiliang. 2019. Service Life Prediction of Precast Concrete Structures Exposed to Chloride Environment. Advances in Civil Engineering،Vol. 2019, no. 2019, pp.1-14.
https://search.emarefa.net/detail/BIM-1115940
نمط استشهاد الجمعية الأمريكية للغات الحديثة (MLA)
Zhang, Dawei…[et al.]. Service Life Prediction of Precast Concrete Structures Exposed to Chloride Environment. Advances in Civil Engineering No. 2019 (2019), pp.1-14.
https://search.emarefa.net/detail/BIM-1115940
نمط استشهاد الجمعية الطبية الأمريكية (AMA)
Zhang, Dawei& Zeng, Yu& Fang, Mingshan& Jin, Weiliang. Service Life Prediction of Precast Concrete Structures Exposed to Chloride Environment. Advances in Civil Engineering. 2019. Vol. 2019, no. 2019, pp.1-14.
https://search.emarefa.net/detail/BIM-1115940
نوع البيانات
مقالات
لغة النص
الإنجليزية
الملاحظات
Includes bibliographical references
رقم السجل
BIM-1115940
قاعدة معامل التأثير والاستشهادات المرجعية العربي "ارسيف Arcif"
أضخم قاعدة بيانات عربية للاستشهادات المرجعية للمجلات العلمية المحكمة الصادرة في العالم العربي
![](/images/ebook-kashef.png)
تقوم هذه الخدمة بالتحقق من التشابه أو الانتحال في الأبحاث والمقالات العلمية والأطروحات الجامعية والكتب والأبحاث باللغة العربية، وتحديد درجة التشابه أو أصالة الأعمال البحثية وحماية ملكيتها الفكرية. تعرف اكثر
![](/images/kashef-image.png)