Electrocatalytic Properties of Calcium Titanate, Strontium Titanate, and Strontium Calcium Titanate Powders Synthesized by Solution Combustion Technique
المؤلفون المشاركون
Jongprateep, Oratai
Sato, Nicha
Techapiesancharoenkij, Ratchatee
Surawathanawises, Krissada
المصدر
Advances in Materials Science and Engineering
العدد
المجلد 2019، العدد 2019 (31 ديسمبر/كانون الأول 2019)، ص ص. 1-7، 7ص.
الناشر
Hindawi Publishing Corporation
تاريخ النشر
2019-04-04
دولة النشر
مصر
عدد الصفحات
7
الملخص EN
Calcium titanate (CaTiO3), strontium titanate (SrTiO3), and strontium calcium titanate (SrxCa1−xTiO3) are widely recognized and utilized as dielectric materials.
Their electrocatalytic properties, however, have not been extensively examined.
The aim of this research is to explore the electrocatalytic performance of calcium titanate, strontium titanate, and strontium calcium titanate, as potential sensing materials.
Experimental results revealed that CaTiO3, SrTiO3, and Sr0.5Ca0.5TiO3 powders synthesized by the solution combustion technique consisted of submicrometer-sized particles with specific surface areas ranging from 4.19 to 5.98 m2/g.
Optical bandgap results indicated that while CaTiO3 and SrTiO3 had bandgap energies close to 3 eV, Sr0.5Ca0.5TiO3 yielded a lower bandgap energy of 2.6 eV.
Cyclic voltammetry tests, measured in 0.1 M sodium nitrite, showed oxidation peaks occurring at 0.58 V applied voltage.
The highest peak current was observed in Sr0.5Ca0.5TiO3 powder.
The superior electrocatalytic performance of Sr0.5Ca0.5TiO3 might be attributed to lower bandgap energy, which consequently facilitates higher electron transfer.
Electrocatalytic performance of Sr0.5Ca0.5TiO3 was subsequently reexamined in a wider concentration range of sodium nitrite.
The results revealed that the material responded linearly to nitrite solution in the range of 0.1 mM to 0.1 M and exhibited sensitivity ranging from 3.117 to 0.040 μA/mM, in the entire tested nitrite concentrations.
The results suggest that Sr0.5Ca0.5TiO3 could also be used for nitrite detection.
نمط استشهاد جمعية علماء النفس الأمريكية (APA)
Jongprateep, Oratai& Sato, Nicha& Techapiesancharoenkij, Ratchatee& Surawathanawises, Krissada. 2019. Electrocatalytic Properties of Calcium Titanate, Strontium Titanate, and Strontium Calcium Titanate Powders Synthesized by Solution Combustion Technique. Advances in Materials Science and Engineering،Vol. 2019, no. 2019, pp.1-7.
https://search.emarefa.net/detail/BIM-1119283
نمط استشهاد الجمعية الأمريكية للغات الحديثة (MLA)
Jongprateep, Oratai…[et al.]. Electrocatalytic Properties of Calcium Titanate, Strontium Titanate, and Strontium Calcium Titanate Powders Synthesized by Solution Combustion Technique. Advances in Materials Science and Engineering No. 2019 (2019), pp.1-7.
https://search.emarefa.net/detail/BIM-1119283
نمط استشهاد الجمعية الطبية الأمريكية (AMA)
Jongprateep, Oratai& Sato, Nicha& Techapiesancharoenkij, Ratchatee& Surawathanawises, Krissada. Electrocatalytic Properties of Calcium Titanate, Strontium Titanate, and Strontium Calcium Titanate Powders Synthesized by Solution Combustion Technique. Advances in Materials Science and Engineering. 2019. Vol. 2019, no. 2019, pp.1-7.
https://search.emarefa.net/detail/BIM-1119283
نوع البيانات
مقالات
لغة النص
الإنجليزية
الملاحظات
Includes bibliographical references
رقم السجل
BIM-1119283
قاعدة معامل التأثير والاستشهادات المرجعية العربي "ارسيف Arcif"
أضخم قاعدة بيانات عربية للاستشهادات المرجعية للمجلات العلمية المحكمة الصادرة في العالم العربي
تقوم هذه الخدمة بالتحقق من التشابه أو الانتحال في الأبحاث والمقالات العلمية والأطروحات الجامعية والكتب والأبحاث باللغة العربية، وتحديد درجة التشابه أو أصالة الأعمال البحثية وحماية ملكيتها الفكرية. تعرف اكثر