The Effects of Ammonium Polyacrylate and Diammonium Citrate as Base and Acid Dispersion Agents on Yttria-Stabilized Zirconia (3Y-TZP)‎ Dispersion Properties

الملخص EN

Stable slurries in dispersions of 3Y-TZP in aqueous suspension with the addition of different concentrations of dispersants such as ammonium polyacrylate (APA) and diammonium citrate (DAC) were investigated.

The dispersion properties were investigated by measuring the particle size, zeta potential, sedimentation, and viscosity as a function of the wt.% of the dispersant.

Both dispersant agents were attached to the 3Y-TZP surface by the carboxylic group, as shown by the FTIR results.

The addition of dispersants was found to produce more dispersed and stabilized aqueous suspension.

As shown the viscosity result, that there is no being viscosity peak has been occurring and viscosity going decrease as the shear rates increasing which mean that the suspension has shear thinning behavior and there is no agglomeration as the shear rate is increased.

It was determined that 3.5 wt.% of DAC and APA produced the best and most stable slurry; when 3.5 wt.% of DAC and APA was added, the zeta potential showed the largest value in the monodisperse condition.

The low pH value of DAC has obtained the higher zeta potential value than APA, which was assumed due to low pH of DAC suspension.

At low pH, the adsorption of the adsorbate will occur in a flat adsorbed, while at higher pH the polyelectrolyte will dangle into solution, thus reducing electrostatic repulsion as it is found in the case of APA addition.

In this condition, the particle size was decreased to the lower value and the slurry’s stability was obtained with the lowest sedimentation height after the sedimentation test for 30 days.

The sample was milled in an attrition mill at 1,000 rpm for four hours.