Surface Corrosion and Microstructure Degradation of Calcium Sulfoaluminate Cement Subjected to Wet-Dry Cycles in Sulfate Solution
المؤلفون المشاركون
Zhang, Wuman
Gong, Sheng
Kang, Bing
المصدر
Advances in Materials Science and Engineering
العدد
المجلد 2017، العدد 2017 (31 ديسمبر/كانون الأول 2017)، ص ص. 1-8، 8ص.
الناشر
Hindawi Publishing Corporation
تاريخ النشر
2017-10-18
دولة النشر
مصر
عدد الصفحات
8
الملخص EN
The hydration products of calcium sulfoaluminate (CSA) cement are different from those of Portland cement.
The degradation of CSA cement subjected to wet-dry cycles in sulfate solution was studied in this paper.
The surface corrosion was recorded and the microstructures were examined by scanning electron microscopy (SEM).
The results show that SO42-, Na+, Mg2+, and Cl− have an effect on the stability of ettringite.
In the initial period of sulfate attack, salt crystallization is the main factor leading to the degradation of CSA cement specimens.
The decomposition and the carbonation of ettringite will cause long-term degradation of CSA cement specimens under wet-dry cycles in sulfate solution.
The surface spalling and microstructure degradation increase significantly with the increase of wet-dry cycles, sulfate concentration, and water to cement ratio.
Magnesium sulfate and sodium chloride reduce the degradation when the concentration of sulfate ions is a constant value.
نمط استشهاد جمعية علماء النفس الأمريكية (APA)
Zhang, Wuman& Gong, Sheng& Kang, Bing. 2017. Surface Corrosion and Microstructure Degradation of Calcium Sulfoaluminate Cement Subjected to Wet-Dry Cycles in Sulfate Solution. Advances in Materials Science and Engineering،Vol. 2017, no. 2017, pp.1-8.
https://search.emarefa.net/detail/BIM-1123550
نمط استشهاد الجمعية الأمريكية للغات الحديثة (MLA)
Zhang, Wuman…[et al.]. Surface Corrosion and Microstructure Degradation of Calcium Sulfoaluminate Cement Subjected to Wet-Dry Cycles in Sulfate Solution. Advances in Materials Science and Engineering No. 2017 (2017), pp.1-8.
https://search.emarefa.net/detail/BIM-1123550
نمط استشهاد الجمعية الطبية الأمريكية (AMA)
Zhang, Wuman& Gong, Sheng& Kang, Bing. Surface Corrosion and Microstructure Degradation of Calcium Sulfoaluminate Cement Subjected to Wet-Dry Cycles in Sulfate Solution. Advances in Materials Science and Engineering. 2017. Vol. 2017, no. 2017, pp.1-8.
https://search.emarefa.net/detail/BIM-1123550
نوع البيانات
مقالات
لغة النص
الإنجليزية
الملاحظات
Includes bibliographical references
رقم السجل
BIM-1123550
قاعدة معامل التأثير والاستشهادات المرجعية العربي "ارسيف Arcif"
أضخم قاعدة بيانات عربية للاستشهادات المرجعية للمجلات العلمية المحكمة الصادرة في العالم العربي
![](/images/ebook-kashef.png)
تقوم هذه الخدمة بالتحقق من التشابه أو الانتحال في الأبحاث والمقالات العلمية والأطروحات الجامعية والكتب والأبحاث باللغة العربية، وتحديد درجة التشابه أو أصالة الأعمال البحثية وحماية ملكيتها الفكرية. تعرف اكثر
![](/images/kashef-image.png)