Very High Cycle Fatigue Crack Initiation Mechanism in Nugget Zone of AA 7075 Friction Stir Welded Joint
المؤلفون المشاركون
Wang, Qingyuan
He, Chao
Kitamura, Kazuhiro
Yang, Kun
Liu, Yong-jie
Chen, Qiang
المصدر
Advances in Materials Science and Engineering
العدد
المجلد 2017، العدد 2017 (31 ديسمبر/كانون الأول 2017)، ص ص. 1-10، 10ص.
الناشر
Hindawi Publishing Corporation
تاريخ النشر
2017-11-27
دولة النشر
مصر
عدد الصفحات
10
الملخص EN
Very high cycle fatigue behavior of nugget zone in AA 7075 friction stir welded joint was experimentally investigated using ultrasonic fatigue testing system (20 kHz) to clarify the crack initiation mechanism.
It was found that the fatigue strength of nugget zone decreased continuously even beyond 107 cycles with no traditional fatigue limits.
Fatigue cracks initiated from the welding defects located at the bottom side of the friction stir weld.
Moreover, a special semicircular zone could be characterized around the crack initiation site, of which the stress intensity factor approximately equaled the threshold of fatigue crack propagation rate.
Finally, a simplified model was proposed to estimate the fatigue life by correlating the welding defect size and applied stress.
The predicted results are in good agreement with the experimental results.
نمط استشهاد جمعية علماء النفس الأمريكية (APA)
He, Chao& Kitamura, Kazuhiro& Yang, Kun& Liu, Yong-jie& Wang, Qingyuan& Chen, Qiang. 2017. Very High Cycle Fatigue Crack Initiation Mechanism in Nugget Zone of AA 7075 Friction Stir Welded Joint. Advances in Materials Science and Engineering،Vol. 2017, no. 2017, pp.1-10.
https://search.emarefa.net/detail/BIM-1124622
نمط استشهاد الجمعية الأمريكية للغات الحديثة (MLA)
He, Chao…[et al.]. Very High Cycle Fatigue Crack Initiation Mechanism in Nugget Zone of AA 7075 Friction Stir Welded Joint. Advances in Materials Science and Engineering No. 2017 (2017), pp.1-10.
https://search.emarefa.net/detail/BIM-1124622
نمط استشهاد الجمعية الطبية الأمريكية (AMA)
He, Chao& Kitamura, Kazuhiro& Yang, Kun& Liu, Yong-jie& Wang, Qingyuan& Chen, Qiang. Very High Cycle Fatigue Crack Initiation Mechanism in Nugget Zone of AA 7075 Friction Stir Welded Joint. Advances in Materials Science and Engineering. 2017. Vol. 2017, no. 2017, pp.1-10.
https://search.emarefa.net/detail/BIM-1124622
نوع البيانات
مقالات
لغة النص
الإنجليزية
الملاحظات
Includes bibliographical references
رقم السجل
BIM-1124622
قاعدة معامل التأثير والاستشهادات المرجعية العربي "ارسيف Arcif"
أضخم قاعدة بيانات عربية للاستشهادات المرجعية للمجلات العلمية المحكمة الصادرة في العالم العربي
تقوم هذه الخدمة بالتحقق من التشابه أو الانتحال في الأبحاث والمقالات العلمية والأطروحات الجامعية والكتب والأبحاث باللغة العربية، وتحديد درجة التشابه أو أصالة الأعمال البحثية وحماية ملكيتها الفكرية. تعرف اكثر