Enhanced Mechanical Properties of Mg-6Sn-3Al-1Zn Alloy with Bimodal Grain Size Disturbed in the Microstructure Uniformly through Changing the Rolling Temperature

الملخص EN

The mechanical properties of Mg-6Sn-3Al-1Zn alloy were enhanced with bimodal grain size disturbed in the microstructure uniformly; the Mg-6Sn-3Al-1Zn alloys were rolled with 60% thickness reduction at different rolling temperatures.

The results have shown that the Mg-6Sn-3Al-1Zn alloys are composed of Mg2Sn phase and α-Mg matrix phase.

When the rolling temperature was less than or equal to 400°C, with the rolling temperature increasing, the average size and volume fraction of Mg2Sn phase and the average grain size of small grains remained unchanged, the average grain size of large grains decreased, the volume fraction of small grains increased, and the yield strength of the alloy increased.

When the rolling temperature reached 450°C, the average size and volume fraction of Mg2Sn phase and the average grain size of large grains increased, and the volume fraction of small grains and the yield strength of the alloy decreased.

The elongation increased with the rolling temperature increasing, but the change trend of hardness was just opposite.

When the alloy was rolled at 400°C, the average sizes of small grains, large grains, and Mg2Sn phases were 3.66 μm, 9.24 μm, and 19.5 μm, respectively.

The volume fractions of small grains, large grains, and Mg2Sn phases were 18.6%, 77.6%, and 3.8%, respectively.

And the tensile properties reached the optimum; for example, the tensile strength, yield strength, elongation, and Vickers hardness were 361 MPa, 289.5 MPa, 20.5%, and 76.3 HV, respectively.