الملخص EN
In this study, the mechanical behaviors, failure characteristics, and microstructure of concrete containing fly ash (FA) against combined freeze-thaw cycles and sulfate attack were studied compared with normal concrete, and the formation rates of corrosion products during coupling cycles were investigated.
Results showed that, during the coupling action of freeze-thaw cycles and sodium sulfate solution, concrete containing 10% fly ash exposed in 5% sodium sulfate solution exhibited better freeze-thaw resistance.
Meanwhile, the variation of compressive strength of concrete during the coupling cycles could be divided into two stages, including the strength enhancement stage and the strength reduction stage.
Moreover, the proportion of micropores and capillary pores decreased obviously during combined freeze-thaw cycles and sulfate attack, and excessive concentration of sodium sulfate solution led to more macropores after high-frequency freeze-thaw cycles.
نمط استشهاد جمعية علماء النفس الأمريكية (APA)
Tian, Wei& Gao, Fangfang. 2020. Damage and Degradation of Concrete under Coupling Action of Freeze-Thaw Cycle and Sulfate Attack. Advances in Materials Science and Engineering،Vol. 2020, no. 2020, pp.1-17.
https://search.emarefa.net/detail/BIM-1129214
نمط استشهاد الجمعية الأمريكية للغات الحديثة (MLA)
Tian, Wei& Gao, Fangfang. Damage and Degradation of Concrete under Coupling Action of Freeze-Thaw Cycle and Sulfate Attack. Advances in Materials Science and Engineering No. 2020 (2020), pp.1-17.
https://search.emarefa.net/detail/BIM-1129214
نمط استشهاد الجمعية الطبية الأمريكية (AMA)
Tian, Wei& Gao, Fangfang. Damage and Degradation of Concrete under Coupling Action of Freeze-Thaw Cycle and Sulfate Attack. Advances in Materials Science and Engineering. 2020. Vol. 2020, no. 2020, pp.1-17.
https://search.emarefa.net/detail/BIM-1129214
نوع البيانات
مقالات
لغة النص
الإنجليزية
الملاحظات
Includes bibliographical references
رقم السجل
BIM-1129214
قاعدة معامل التأثير والاستشهادات المرجعية العربي "ارسيف Arcif"
أضخم قاعدة بيانات عربية للاستشهادات المرجعية للمجلات العلمية المحكمة الصادرة في العالم العربي
تقوم هذه الخدمة بالتحقق من التشابه أو الانتحال في الأبحاث والمقالات العلمية والأطروحات الجامعية والكتب والأبحاث باللغة العربية، وتحديد درجة التشابه أو أصالة الأعمال البحثية وحماية ملكيتها الفكرية. تعرف اكثر