Theoretical Analysis and Experimental Research into the Mechanical Properties of Al-Ti-Al Symmetrical Laminated Plate

الملخص EN

In order to have both the surface corrosion resistance of aluminum alloy and the high specific strength characteristics of titanium alloy, titanium alloy TC4, and aluminum alloy 6061 can be used to make aluminum-titanium-aluminum (Al-Ti-Al) three-layer laminated plate by hot rolling.

In this paper, the classical laminated plate theory was used to calculate the stiffness, specific stiffness, strength, and specific strength of the laminated plate.

The results showed that when the coating rate of titanium alloy TC4 was 0.5, bending specific stiffness and bending specific strength were the minimum, but all other parameters increased with the increase of the coating rate of titanium alloy TC4.

Therefore, in actual production, the coating rate of titanium alloy should be avoided being 0.5.

Then, the rolling experiments of the Al-Ti-Al laminated plate were carried out with different temperatures, reduction rates, and thickness ratios.

Finally, the tensile test and energy spectrum analysis of the laminated plate were carried out.

The results showed that, with the increase of rolling temperature, the tensile strength, the extensibility, and the thickness of the diffusion layer increased; if the coating rate of titanium alloy TC4 was between 0.2 and 0.33, the mechanical properties, the bonding strength, and the thickness of the diffusion layer increased with the increase of the coating rate of titanium alloy TC4.