Effect of Disinfectants on Mechanical Properties of Orthodontic Acrylics

الملخص EN

Objective.

Infection control protocols in dentistry dictate that orthodontic acrylics have to be disinfected.

No specific products for orthodontic acrylics are available.

The objective of this study was to investigate the influence of chemical disinfectants on mechanical properties of orthodontic acrylics.

Materials and Methods.

260 test specimens of two cold-curing orthodontic acrylics were manufactured.

Three chemical disinfecting agents were tested: Impresept, D050 Instru-Gen, and Stammopur DR.

Test specimens were stored in distilled water and divided into test groups.

E-Modulus, flexural strength, macro hardness, micro hardness, average roughness, and colour change were measured.

Results.

Disinfection agents showed no significant influence on E-modulus.

Values ranged from 1783.80 ± 163.80 MPa (Forestacryl colourless) to 2474.00 ± 135.00 MPa (Orthocryl green) after storage in distilled water.

Disinfection agents performed no significant influence on flexural strength.

Values ranged from 18.64±1.59 N/mm2 (Forestacryl colourless) to 25.64 ± 1.43 N/mm2 (Orthocryl green) after storage in distilled water.

Orthocryl colourless showed a reduction of the macro hardness after disinfection (Stammopur DR (p≤0.001), D050 Instru-Gen (p≤0.037)).

Disinfection of Orthocryl green with D050 Instru-Gen (p<0.001) and Forestacryl colourless with Impresept (p≤0.001) led to a reduction of macro hardness.

Micro hardness of Orthocryl colourless altered significantly after disinfection with D050 Instru-Gen (p≤0.001).

Micro hardness of Forestacryl colourless increased (Impresept (p≤0.039)) and decreased (Stammopur DR (p≤0.006) Instru-Gen (p≤0.001)) after disinfection.

Average roughness did not change significantly (Orthocryl colourless).

Forestacryl colourless performed a significant change after disinfection with Stammopur DR (p≤0.05).

This is also true for the disinfection of Orthocryl green and Forestacryl pink with Instru-Gen (p≤0.05).

Disinfection performed no significant influence on colour change.

ΔE-values were in a range of 1 to 2.

Conclusions.

Some orthodontic acrylics disinfection caused significant changes of determined parameters.

Changes were specific for the applied disinfectant and tested orthodontic acrylic.

Further studies should verify the impact of long-term disinfection intervals.

Thus, from manufacturers of orthodontic acrylics recommendations for appropriate disinfectants would be desirable.