Corrosion Failure of AISI4340 Steel in Oxygen-Containing Aqueous Chloride Solution

الملخص EN

Stress corrosion cracking behavior of 4340 steel in oxygen-containing or chloride containing aqueous solution was researched, the tensile experiment results indicated 100°C deaerated distilled water, the rupture of 4340 steel mainly belongs to ductile fracture, the addition of oxygen or chloride would increase the SCC tendency of 4340 steel and transformed the rupture mechanism from ductile fracture to brittle rupture, the existence of oxygen or chloride would decrease KISCC of 4340 steel in 100°C aqueous solution slightly, the simultaneous action of oxygen and chloride existed, and the simultaneous action would further increase the SCC tendency of 4340 steel in aqueous solution.