Tuning Anatase-Rutile Phase Transition Temperature: TiO2SiO2 Nanoparticles Applied in Dye-Sensitized Solar Cells

الملخص EN

TiO2/SiO2 nanoparticles with 3, 5, and 10 molar percent of silica, were synthesized by hydrothermal method and characterized by SEM, TEM, N2 adsorption-desorption isotherms, X-ray diffraction, and Raman and UV-Vis spectroscopy.

While pristine TiO2 thermally treated at 500°C presents a surface area of 36 m2 g-1 (±10 m2 g-1), TiO2/SiO2 containing 3, 5, and 10 molar percent of silica present surface areas of 93, 124, and 150 m2 g-1 (±10 m2 g-1), respectively.

SiO2 is found to form very small amorphous domains well dispersed in the TiO2 matrix.

X-ray diffraction and Raman spectroscopy data show that anatase-to-rutile phase transition temperature is delayed by the presence of SiO2, enabling single-anatase phase photoanodes for DSSCs.

According to the I×V measurements, photoanodes with 3% of SiO2 result in improved efficiency, which is mainly related to increased surface area and dye loading.

In addition, the results suggest a gain in photocurrent related to the passivation of defects by SiO2.