Thermal Stability and Flame Resistance of the Coextruded Wood-Plastic Composites Containing Talc-Filled Plastic Shells
المؤلفون المشاركون
Wu, Qinglin
Huang, Runzhou
Zhang, Xian
Chen, Zhilin
Wan, Minli
المصدر
International Journal of Polymer Science
العدد
المجلد 2020، العدد 2020 (31 ديسمبر/كانون الأول 2020)، ص ص. 1-9، 9ص.
الناشر
Hindawi Publishing Corporation
تاريخ النشر
2020-07-01
دولة النشر
مصر
عدد الصفحات
9
التخصصات الرئيسية
الملخص EN
Talc is a popular filler for the fabrication of plastic composites.
The presence of talc helps improve mechanical, thermal, and flame resistance properties of the composite.
In this work, we report the influence of a talc-filled plastic shell layer on thermal stability and fire flammability of the core-shell structured wood high-density polyethylene (HDPE) composites manufactured through coextrusion.
The result showed that morphological analysis of the char layer after combustion confirmed the formation of a continuous surface char layer with talc addition in the composites, helping block fire penetration and enhance overall fire resistance of the composites.
The shell thickness averaged at 1.0±0.2 mm, which represents a fair thick shell over a 10 mm thick WPC core layer.
The surface of regular wood-filled HDPE showed large cracks, allowing more rapid fire penetration and reducing its fire resistance.
At 800°C, average residual weight for all composite was 21.5±13.8%, most of which was attributed to the inorganic nonvolatile talc components.
With the increase of talc level, THR values of coextruded WPC decreased from 302.47 MJ/m2 (5 wt% of talc) to 262.96 kW/m2 (50 wt% of talc).
When talc content in the shell layer was less than 25 wt%, the flame resistance properties were slightly enhanced compared with the composites containing unmodified HDPE shells.
When talc content in the shell exceeded 25 wt%, the composite’s total heat release and its rate substantially decreased.
نمط استشهاد جمعية علماء النفس الأمريكية (APA)
Huang, Runzhou& Zhang, Xian& Chen, Zhilin& Wan, Minli& Wu, Qinglin. 2020. Thermal Stability and Flame Resistance of the Coextruded Wood-Plastic Composites Containing Talc-Filled Plastic Shells. International Journal of Polymer Science،Vol. 2020, no. 2020, pp.1-9.
https://search.emarefa.net/detail/BIM-1173716
نمط استشهاد الجمعية الأمريكية للغات الحديثة (MLA)
Huang, Runzhou…[et al.]. Thermal Stability and Flame Resistance of the Coextruded Wood-Plastic Composites Containing Talc-Filled Plastic Shells. International Journal of Polymer Science No. 2020 (2020), pp.1-9.
https://search.emarefa.net/detail/BIM-1173716
نمط استشهاد الجمعية الطبية الأمريكية (AMA)
Huang, Runzhou& Zhang, Xian& Chen, Zhilin& Wan, Minli& Wu, Qinglin. Thermal Stability and Flame Resistance of the Coextruded Wood-Plastic Composites Containing Talc-Filled Plastic Shells. International Journal of Polymer Science. 2020. Vol. 2020, no. 2020, pp.1-9.
https://search.emarefa.net/detail/BIM-1173716
نوع البيانات
مقالات
لغة النص
الإنجليزية
الملاحظات
Includes bibliographical references
رقم السجل
BIM-1173716
قاعدة معامل التأثير والاستشهادات المرجعية العربي "ارسيف Arcif"
أضخم قاعدة بيانات عربية للاستشهادات المرجعية للمجلات العلمية المحكمة الصادرة في العالم العربي
تقوم هذه الخدمة بالتحقق من التشابه أو الانتحال في الأبحاث والمقالات العلمية والأطروحات الجامعية والكتب والأبحاث باللغة العربية، وتحديد درجة التشابه أو أصالة الأعمال البحثية وحماية ملكيتها الفكرية. تعرف اكثر