The Effect of Irradiation with a 405 nm Blue-Violet Laser on the Bacterial Adhesion on the Osteosynthetic Biomaterials

الملخص EN

Delayed postoperative infection is known as a major complication after bone surgeries using osteosynthetic biomaterial such as titanium (Ti) and bioresorbable organic materials.

However, the precise cause of this type of infection is still unclear and no effective prevention has been established.

The purpose of this study is to investigate the effect of irradiation with a 405 nm blue-violet laser on the bacteria adhered on the Ti and hydroxyapatite-poly-L-lactic acid- (HA-PLLA) based material surfaces and to verify the possibility of its clinical application to prevent the delayed postoperative infection after bone surgeries using osteosynthetic biomaterial.

The suspension of Staphylococcus aureus FDA 209P was delivered onto the surface of disks composed of Ti or HA-PLLA.

Bacterial adhesion on each disk was observed using a scanning electron microscope (SEM).

After thorough washing with distilled water, the growth of bacteria attached to the material surfaces was examined with an alamar blue-based redox indicator.

Moreover, a bactericidal effect of 405 nm blue-violet laser irradiation on residual bacteria on both materials was investigated using colony-forming assay.

As a result, there was no significant difference in the bacterial adhesion between Ti and HA-PLLA materials.

In contrast, 45 J/cm2 of irradiation with 405 nm blue-violet laser inhibited the bacterial growth at approximately 93% on Ti disks and at approximately 99% on HA-PLLA disks.

This study clearly demonstrated the possibility that the irradiation with a 405 nm blue-violet laser is useful as an alternative management strategy for the prevention of delayed postoperative infection after bone surgeries using osteosynthetic biomaterials.