Study on Mechanical Properties and Fire Resistance of Epoxy Nanocomposite Reinforced with Environmentally Friendly Additive: Nanoclay I.30E
المؤلفون المشاركون
Nguyen, Tuan Anh
Pham, Thi Mai Huong
Dang, Thi Huong
Do, Thi Hanh
Nguyen, Quang Tung
المصدر
العدد
المجلد 2020، العدد 2020 (31 ديسمبر/كانون الأول 2020)، ص ص. 1-13، 13ص.
الناشر
Hindawi Publishing Corporation
تاريخ النشر
2020-04-30
دولة النشر
مصر
عدد الصفحات
13
التخصصات الرئيسية
الملخص EN
The main purpose of this study is to complete the research process of dispersing nanoclay I.30E (montmorillonite) into epoxy Epikote 240 by mechanical method combined with energy-saving ultrasonic method.
We investigate appropriate dispersion conditions such as stirring speed, mechanical stirring temperature, ultrasonic stirring time, and ultrasonic stirring capacity, which affect the mechanical properties and fire resistance of nanocomposite materials.
The nanoclay contents studied were 1, 2, 3, and 4% by weight, and the methods used in this study are FE-SEM; XRD; and flame-retardant evaluation methods: LOI, UL 94HB.
The mechanical properties were studied: tensile strength, flexural strength, compression strength, and impact resistance Izod.
The dispersion method was recommended to stir mechanically at a speed of 3000 rpm at 80°C for 8 hours and then conduct ultrasonic vibrations for 6 hours at 65°C.
The results showed that epoxy Epikote 240/nanoclay I.30E nanocomposite material had mechanical properties and improved fire retardancy with a small amount of nanoclay I.30E added (2% by weight): tensile strength of 63.5 MPa (increased by 13.59%), flexural strength of 116.80 MPa (increased by 34.63%), compressive strength of 179.67 MPa (increased by 15.11%), impact resistance Izod of 12.81 KJ/m2 (increased by 80.16%), oxygen limit of 23.7%, and combustion rate of 24.5 mm/min; according to UL 94HB, the combustion rate reached 22.59 mm/min.
نمط استشهاد جمعية علماء النفس الأمريكية (APA)
Nguyen, Tuan Anh& Pham, Thi Mai Huong& Dang, Thi Huong& Do, Thi Hanh& Nguyen, Quang Tung. 2020. Study on Mechanical Properties and Fire Resistance of Epoxy Nanocomposite Reinforced with Environmentally Friendly Additive: Nanoclay I.30E. Journal of Chemistry،Vol. 2020, no. 2020, pp.1-13.
https://search.emarefa.net/detail/BIM-1181617
نمط استشهاد الجمعية الأمريكية للغات الحديثة (MLA)
Nguyen, Tuan Anh…[et al.]. Study on Mechanical Properties and Fire Resistance of Epoxy Nanocomposite Reinforced with Environmentally Friendly Additive: Nanoclay I.30E. Journal of Chemistry No. 2020 (2020), pp.1-13.
https://search.emarefa.net/detail/BIM-1181617
نمط استشهاد الجمعية الطبية الأمريكية (AMA)
Nguyen, Tuan Anh& Pham, Thi Mai Huong& Dang, Thi Huong& Do, Thi Hanh& Nguyen, Quang Tung. Study on Mechanical Properties and Fire Resistance of Epoxy Nanocomposite Reinforced with Environmentally Friendly Additive: Nanoclay I.30E. Journal of Chemistry. 2020. Vol. 2020, no. 2020, pp.1-13.
https://search.emarefa.net/detail/BIM-1181617
نوع البيانات
مقالات
لغة النص
الإنجليزية
الملاحظات
Includes bibliographical references
رقم السجل
BIM-1181617
قاعدة معامل التأثير والاستشهادات المرجعية العربي "ارسيف Arcif"
أضخم قاعدة بيانات عربية للاستشهادات المرجعية للمجلات العلمية المحكمة الصادرة في العالم العربي
![](/images/ebook-kashef.png)
تقوم هذه الخدمة بالتحقق من التشابه أو الانتحال في الأبحاث والمقالات العلمية والأطروحات الجامعية والكتب والأبحاث باللغة العربية، وتحديد درجة التشابه أو أصالة الأعمال البحثية وحماية ملكيتها الفكرية. تعرف اكثر
![](/images/kashef-image.png)