The Influence of Spherical Nano-SiO2 Content on the Thermal Protection Performance of Thermal Insulation Ablation Resistant Coated Fabrics

الملخص EN

In the high temperatures experienced in fire, radiant heat accounts for 80% of the total heat flow; therefore, improving the radiation protection is the best way to enhance the thermal protective performance of thermal insulation ablation resistant coated fabrics.

To achieve this goal, the coating process and the ingredients used were optimized, spherical nano-SiO2 and other particles were added, and thermal insulation ablation resistant coated fabrics with high radiant heat reflectivity were prepared.

The influence of the spherical nano-SiO2 content on the thermal protection performance of the prepared coated fabrics was investigated.

Research showed that (1) the radiant heat reflectivity of the prepared coated fabrics improves significantly with increasing content of spherical nano-SiO2; when the mass fraction of spherical nano-SiO2 is 15%, the reflectivity of coated fabrics is at its largest, and its average value was 74.30%.

At present, the average size of grains in samples increased 1.9 times; (2) after adding the spherical nano-SiO2, the thermal stability of the thermal insulation ablation resistant coated fabrics is significantly improved; the residual mass is as high as 88.49% at 1200°C, which is 18.77% higher than the residual mass of the coated fabrics with no spherical nano-SiO2 added at the same temperature.