Gelatin Template Synthesis of Aluminum Oxide andor Silicon Oxide Containing MicroMesopores Using the Proteic Sol-Gel Method

الملخص EN

Aluminum oxide and/or silicon oxide-based supports were synthesized by proteic sol-gel method.

The characterization was performed through the analysis of TG, XRD, FTIR, SEM, and N2 physisorption.

The XRD diffractograms showed an amorphous material profile.

TG results indicate the total liberation of the organic and inorganic material in the calcination temperature used, occurring in different mass loss range.

This piece of information was reaffirmed by the FTIR spectra, which presented characteristic bands of gelatin structure before calcinations which disappear in the spectrum of the solid after calcinations, indicating the loss of organic matter from gelatin after heat treatment.

The spectra exhibited M-O stretching vibration at low wavenumbers after calcinations related to metal oxides.

The acquired images by SEM suggest the obtaining of a highly porous material with very different characteristics depending on the composition of the support.

The N2 isotherms indicate the presence of a micro/mesoporous oxide with interesting textural properties, particularly for the supports containing aluminum and silicon oxide.

The ethanol dehydration results showed greater selectivity to diethyl ether compared to ethylene.

From the reaction data, the following order of acid strength was obtained: 2Si-Al > Si-2Al > Si-Al > Al, which is related to the Si-Al ratio.