Urea-Assisted Synthesis of Nanospherical and Plate-Like Magnesium Oxides for Efficient Removal of Reactive Dye Wastes

الملخص EN

Nanospherical and plate-like magnesium oxide has been successfully synthesized by urea precipitation method for the first time.

A magnesium oxide precursor was prepared by heating MgCl2 solution with urea for 12 hours at 90°C.

Then the calcined precursor was analysed by Scanning electron microscopy (SEM), X-ray diffraction (XRD), Fourier transform infrared (FT-IR) spectroscopy, thermogravimetric analysis (TGA), and high-resolution transmission electron microscopy (HR-TEM).

In the presence of the nonionic surfactant Triton X-100 in the system, the reaction yielded in nanospheres of MgO contrast to the plate-like MgO in the absence of the surfactant.

The precursor and the calcined product appeared in similar morphologies under SEM in both cases with a slight reduction of size upon calcination.

The final product was confirmed as MgO using XRD and FT-IR spectroscopic methods.

In TGA, both samples showed similar mass loss values upon elimination of adsorbed water molecules and decomposition of the precursor into MgO; however, the nanospherical MgO sample showed an additional weight loss due to elimination of the associated surfactant molecules.

The efficiency of removing reactive dye wastes was quantified by UV-visible spectroscopy using reactive yellow dye.

Plate-like MgO showed a porous structure under HR-TEM analysis in the dye adsorption study, and both plate-like and nanospherical MgO showed good dye adsorption capability.

MgO nanospheres showed higher capacity of dye adsorption compared to plate-like MgO, explained by its higher surface are-to-volume ratio, while the plate-like MgO also performed well due to having a nanoporous structure.

These nanomaterials will offer high potential in purifying waste water and as well in recovering expensive dye products.