On the Structural, Morphological, and Electrical Properties of Carbon Nanowalls Obtained by Plasma-Enhanced Chemical Vapor Deposition

الملخص EN

In this study, we investigated the morphological, structural, and electrical properties of carbon nanowall (CNW) structures obtained by plasma-enhanced chemical vapour deposition (PECVD) and underlined the induced effects of argon/nitrogen (Ar/N2) postsynthesis plasma treatment on the electrical behaviour.

The top view and cross-section scanning electron microscopy micrographs revealed that the fabricated samples are about 18 μm height, and the edges are less than 10 nm.

The Raman analysis showed the presence of the specific peaks of graphene-based materials, i.e., D-band, G-band, D′-band, 2D-band, and D+G-band.

The average values of the electrical resistance of fabricated samples were evaluated by current-voltage characteristics acquired at room temperature, in the ranges of 0 V–0.2 V, and an increase was noticed with about 50% after the Ar/N2 postsynthesis plasma treatment compared to pristine samples.

Moreover, the Hall measurements proved that the obtained CNW structures had p-type conductivity (Hall coefficient was 0.206 m3/C), and the concentration of charge carriers was 7.8×1019 cm-3, at room temperature.