Effect of Alternate Corrosion and Fatigue on Fatigue Crack Growth Characterization of 2024-T4 Aluminum Alloy
المؤلفون المشاركون
Li, Changfan
He, Yuting
Zhang, Sheng
Zhang, Teng
Zhang, Tianyu
المصدر
Mathematical Problems in Engineering
العدد
المجلد 2020، العدد 2020 (31 ديسمبر/كانون الأول 2020)، ص ص. 1-15، 15ص.
الناشر
Hindawi Publishing Corporation
تاريخ النشر
2020-03-12
دولة النشر
مصر
عدد الصفحات
15
التخصصات الرئيسية
الملخص EN
To investigate the effect of alternate corrosion and fatigue on fatigue crack growth characterization of 2024-T4 aluminum alloy, the pure fatigue test, “corrosion + fatigue” test (commonly known as pre-corrosion fatigue), and the “fatigue + corrosion + fatigue” alternating test of single-sided notched specimen of 2024-T4 aluminum alloy were carried out.
The fatigue crack life of alternate corrosion and fatigue is longer than that of the pre-corrosion fatigue when the corrosion time is the same.
And the more the times of alternating, the longer the crack growth life will be.
This is mainly because the fatigue crack growth rate will change suddenly, which will have a certain hysteresis effect on the fatigue crack growth.
The corrosion and fracture morphology characteristics of the alternate test were examined by scanning electron microscopy (SEM), and the composition of corrosion products was examined by the energy dispersion spectrum (EDS).
The prediction model of fatigue crack growth rate considering the alternating hysteresis effect of corrosion and fatigue based on the Paris formula was established, and the parameters and precision of the model were calculated and verified.
The results show that the model has certain engineering application value.
نمط استشهاد جمعية علماء النفس الأمريكية (APA)
Zhang, Tianyu& He, Yuting& Li, Changfan& Zhang, Teng& Zhang, Sheng. 2020. Effect of Alternate Corrosion and Fatigue on Fatigue Crack Growth Characterization of 2024-T4 Aluminum Alloy. Mathematical Problems in Engineering،Vol. 2020, no. 2020, pp.1-15.
https://search.emarefa.net/detail/BIM-1197892
نمط استشهاد الجمعية الأمريكية للغات الحديثة (MLA)
Zhang, Tianyu…[et al.]. Effect of Alternate Corrosion and Fatigue on Fatigue Crack Growth Characterization of 2024-T4 Aluminum Alloy. Mathematical Problems in Engineering No. 2020 (2020), pp.1-15.
https://search.emarefa.net/detail/BIM-1197892
نمط استشهاد الجمعية الطبية الأمريكية (AMA)
Zhang, Tianyu& He, Yuting& Li, Changfan& Zhang, Teng& Zhang, Sheng. Effect of Alternate Corrosion and Fatigue on Fatigue Crack Growth Characterization of 2024-T4 Aluminum Alloy. Mathematical Problems in Engineering. 2020. Vol. 2020, no. 2020, pp.1-15.
https://search.emarefa.net/detail/BIM-1197892
نوع البيانات
مقالات
لغة النص
الإنجليزية
الملاحظات
Includes bibliographical references
رقم السجل
BIM-1197892
قاعدة معامل التأثير والاستشهادات المرجعية العربي "ارسيف Arcif"
أضخم قاعدة بيانات عربية للاستشهادات المرجعية للمجلات العلمية المحكمة الصادرة في العالم العربي
تقوم هذه الخدمة بالتحقق من التشابه أو الانتحال في الأبحاث والمقالات العلمية والأطروحات الجامعية والكتب والأبحاث باللغة العربية، وتحديد درجة التشابه أو أصالة الأعمال البحثية وحماية ملكيتها الفكرية. تعرف اكثر