Correlation between Fracture Morphology and Microstructural Evolution during Long-Term Aging of EK61 Superalloy
المؤلفون المشاركون
Huang, Jin
Xu, Guohua
Qin, Heyong
Zheng, Lei
المصدر
العدد
المجلد 2020، العدد 2020 (31 ديسمبر/كانون الأول 2020)، ص ص. 1-8، 8ص.
الناشر
Hindawi Publishing Corporation
تاريخ النشر
2020-04-24
دولة النشر
مصر
عدد الصفحات
8
التخصصات الرئيسية
تكنولوجيا المعلومات وعلم الحاسوب
الملخص EN
Microstructural evolutions of EK61 superalloy during long-term aging until 1000 h at 700°C and 750°C, respectively, are studied by combination of Scanning Electron Microscope (SEM) and Transmission Electron Microscope (TEM).
Impact fracture morphologies after aging for different time are observed by the SEM.
The microstructure is found to be relatively stable during aging at 700°C, and the fracture morphologies are characterized by transgranular fracture.
At 750°C, the coarsening of γ′ phase leads the reduction of the quantity of dimples, the chainization of carbides on grain boundaries leads to intergranular fracture, and the netting of η phases within grains leads to the formation of lamellar cleavage steps.
It is obvious that the destabilization of precipitated phases affects fracture morphology significantly.
The relationship between fracture morphology and the microstructure promotes the evaluation of service reliability of EK61 superalloy.
نمط استشهاد جمعية علماء النفس الأمريكية (APA)
Huang, Jin& Xu, Guohua& Qin, Heyong& Zheng, Lei. 2020. Correlation between Fracture Morphology and Microstructural Evolution during Long-Term Aging of EK61 Superalloy. Scanning،Vol. 2020, no. 2020, pp.1-8.
https://search.emarefa.net/detail/BIM-1207387
نمط استشهاد الجمعية الأمريكية للغات الحديثة (MLA)
Huang, Jin…[et al.]. Correlation between Fracture Morphology and Microstructural Evolution during Long-Term Aging of EK61 Superalloy. Scanning No. 2020 (2020), pp.1-8.
https://search.emarefa.net/detail/BIM-1207387
نمط استشهاد الجمعية الطبية الأمريكية (AMA)
Huang, Jin& Xu, Guohua& Qin, Heyong& Zheng, Lei. Correlation between Fracture Morphology and Microstructural Evolution during Long-Term Aging of EK61 Superalloy. Scanning. 2020. Vol. 2020, no. 2020, pp.1-8.
https://search.emarefa.net/detail/BIM-1207387
نوع البيانات
مقالات
لغة النص
الإنجليزية
الملاحظات
Includes bibliographical references
رقم السجل
BIM-1207387
قاعدة معامل التأثير والاستشهادات المرجعية العربي "ارسيف Arcif"
أضخم قاعدة بيانات عربية للاستشهادات المرجعية للمجلات العلمية المحكمة الصادرة في العالم العربي
تقوم هذه الخدمة بالتحقق من التشابه أو الانتحال في الأبحاث والمقالات العلمية والأطروحات الجامعية والكتب والأبحاث باللغة العربية، وتحديد درجة التشابه أو أصالة الأعمال البحثية وحماية ملكيتها الفكرية. تعرف اكثر