Surface Characterization and Corrosion Resistance of Biomedical AZ31 Mg Alloy Treated by Microarc Fluorination

الملخص EN

The application prospect of biodegradable materials is being studied extensively.

However, the high corrosion rate and its alloys in body fluids have been major limitations of the application of pure Mg (magnesium).

To improve corrosion resistance of biodegradable AZ31 Mg alloy, we adopted microarc fluorination within a voltage range of 100-300 V in 46% hydrofluoric acid.

To obtain morphologies, chemical compositions, and structural characteristics, field-emission scanning electron microscopy (FE-SEM), energy-dispersive X-ray spectroscopy (EDS), and X-ray diffraction (XRD) were performed, respectively.

Results showed that the coating was mainly composed of MgF2.

Electrochemical corrosion and immersion tests proved that the corrosion resistance of MAF-treated AZ31 Mg alloy was significantly improved compared with untreated AZ31 Mg alloy in HBSS (Hank’s Balanced Salt Solution).

Current densities of AZ31, MAF100, MAF150, MAF200, MAF250, and MAF300 were 342.4, 0.295, 0.228, 0.177, 0.199, and 0.212 μA/cm2, respectively.

The roughness test indicated that samples under MAF treatment of 200 V, 250 V, and 300 V had large surface roughness.

Meanwhile, the contact angle measurement and surface free energy test suggested that those samples had smaller contact angle and higher SFE than Ti.

Thus, MAF-treated AZ31 Mg alloy might have promising application in various fields.