Infeluence of high temperature treatement on aircooled slag - dealuminated kaolin compositecement pastes
المؤلف
المصدر
Housing and Building National Research Center Journal
العدد
المجلد 6، العدد 2 (31 أغسطس/آب 2010)، ص ص. 8-16، 9ص.
الناشر
المركز القومي لبحوث الإسكان و البناء
تاريخ النشر
2010-08-31
دولة النشر
مصر
عدد الصفحات
9
التخصصات الرئيسية
العلوم الهندسية والتكنولوجية (متداخلة التخصصات)
الموضوعات
الملخص EN
This article aims to study the effect of temperature on the air-cooled slag-dealuminated kaolin composite cement pastes up to 800 oC.
Pozzolanic cement was prepared from 80 wt % ordinary Portland cement (OPC) and 20 wt % air-cooled slag.
The air-cooled slag was partially substituted by dealuminated kaolin (DAK) to prepare composite cement.
The results revealed that the standard water of consistency increases with increasing dealuminated kaolin content due to the increase of its surface area.
Cement paste made with 5 wt.
% dealuminated kaolin shows an acceleration of the initial setting time due to the nucleating effect and lor accurring dealuminated kaolin which increases the initial setting time of composite cement pastes is accelerated due to the higher activity of DAK in comparison with ACS.
However, the final setting time of composite cement pastes is retardered with up to 15 wt.
% DAK due to the increase of mixing water.
On the other side, 20 wt.
% DAK accelerates the initial and final setting times and decreases the liberated lime content as a result of its consumption by DAK hydration.
The effect of heat treatment was carried out by determining the ignition loss, bulk density, total porosity and compressive strength for the hardened cement pastes.
The products of thermally treated composite cement pastes were identified by using XRD techniques and visual inspection.
نمط استشهاد جمعية علماء النفس الأمريكية (APA)
al-Sukkari, Tariq M.. 2010. Infeluence of high temperature treatement on aircooled slag - dealuminated kaolin compositecement pastes. Housing and Building National Research Center Journal،Vol. 6, no. 2, pp.8-16.
https://search.emarefa.net/detail/BIM-122580
نمط استشهاد الجمعية الأمريكية للغات الحديثة (MLA)
al-Sukkari, Tariq M.. Infeluence of high temperature treatement on aircooled slag - dealuminated kaolin compositecement pastes. Housing and Building National Research Center Journal Vol. 6, no. 2 (Aug. 2010), pp.8-16.
https://search.emarefa.net/detail/BIM-122580
نمط استشهاد الجمعية الطبية الأمريكية (AMA)
al-Sukkari, Tariq M.. Infeluence of high temperature treatement on aircooled slag - dealuminated kaolin compositecement pastes. Housing and Building National Research Center Journal. 2010. Vol. 6, no. 2, pp.8-16.
https://search.emarefa.net/detail/BIM-122580
نوع البيانات
مقالات
لغة النص
الإنجليزية
الملاحظات
Includes bibliographical references : p. 16
رقم السجل
BIM-122580
قاعدة معامل التأثير والاستشهادات المرجعية العربي "ارسيف Arcif"
أضخم قاعدة بيانات عربية للاستشهادات المرجعية للمجلات العلمية المحكمة الصادرة في العالم العربي
![](/images/ebook-kashef.png)
تقوم هذه الخدمة بالتحقق من التشابه أو الانتحال في الأبحاث والمقالات العلمية والأطروحات الجامعية والكتب والأبحاث باللغة العربية، وتحديد درجة التشابه أو أصالة الأعمال البحثية وحماية ملكيتها الفكرية. تعرف اكثر
![](/images/kashef-image.png)