Fracture toughness of glass infiltrated (3Y-TZP Al2O3) composite
المؤلفون المشاركون
Ibrahim, Sarah Nabil
Zaidan, Shihab A.
Muhammad, Mudhafar A.
المصدر
Engineering and Technology Journal
العدد
المجلد 39، العدد 1B (31 يناير/كانون الثاني 2021)، ص ص. 141-149، 9ص.
الناشر
تاريخ النشر
2021-01-31
دولة النشر
العراق
عدد الصفحات
9
التخصصات الرئيسية
الموضوعات
الملخص EN
Five different 3 mol.
% yttria-tetragonal zirconia polycrystals/alumina (3Y-TZP/Al2O3) -glass specimens have been fabricated by the glass infiltration method.
graphite additives were added to the (3Y-TZP/20Wt.
% Al2O3) to obtain porous structure.
The ATZ (Alumina Toughened Zirconia) skeleton have prepared by the normal compaction method.
The specimen had been infiltrated by the glass (18Wt.
% lithium hydroxide, 72 wt.
% feldspar, and 10Wt.
% nano Titanium oxide) at 1185ᵒC.
Results showed that the porosity of (3Y-TZP/Al2O3) composite was increased while bulk density decreased with increasing graphite additives.
The elastic modulus of (3Y-TZP/Al2O3)-glass was decreased (159-109GPa) with increasing the amount of glass infiltrated.
Hardness was constant for all the specimens in value of (5.66 GPa), while increment of materials fracture toughening was due to the increasing the glass weight fraction, the kIc was lied between (0.53-1.
54MPa.
m1/2).
The glass infiltrated (3Y-TZP/Al2O3) process was successfully increased the fracture toughness by penetrated different amounts of glass into the (3Y-TZP/Al2O3) structure.
نمط استشهاد جمعية علماء النفس الأمريكية (APA)
Ibrahim, Sarah Nabil& Zaidan, Shihab A.& Muhammad, Mudhafar A.. 2021. Fracture toughness of glass infiltrated (3Y-TZP Al2O3) composite. Engineering and Technology Journal،Vol. 39, no. 1B, pp.141-149.
https://search.emarefa.net/detail/BIM-1282622
نمط استشهاد الجمعية الأمريكية للغات الحديثة (MLA)
Ibrahim, Sarah Nabil…[et al.]. Fracture toughness of glass infiltrated (3Y-TZP Al2O3) composite. Engineering and Technology Journal Vol. 39, no. 1B (2021), pp.141-149.
https://search.emarefa.net/detail/BIM-1282622
نمط استشهاد الجمعية الطبية الأمريكية (AMA)
Ibrahim, Sarah Nabil& Zaidan, Shihab A.& Muhammad, Mudhafar A.. Fracture toughness of glass infiltrated (3Y-TZP Al2O3) composite. Engineering and Technology Journal. 2021. Vol. 39, no. 1B, pp.141-149.
https://search.emarefa.net/detail/BIM-1282622
نوع البيانات
مقالات
لغة النص
الإنجليزية
الملاحظات
Includes bibliographical references : p. 148-149
رقم السجل
BIM-1282622
قاعدة معامل التأثير والاستشهادات المرجعية العربي "ارسيف Arcif"
أضخم قاعدة بيانات عربية للاستشهادات المرجعية للمجلات العلمية المحكمة الصادرة في العالم العربي
تقوم هذه الخدمة بالتحقق من التشابه أو الانتحال في الأبحاث والمقالات العلمية والأطروحات الجامعية والكتب والأبحاث باللغة العربية، وتحديد درجة التشابه أو أصالة الأعمال البحثية وحماية ملكيتها الفكرية. تعرف اكثر